CN106183309A - A kind of feather dress fabric - Google Patents
A kind of feather dress fabric Download PDFInfo
- Publication number
- CN106183309A CN106183309A CN201610568129.1A CN201610568129A CN106183309A CN 106183309 A CN106183309 A CN 106183309A CN 201610568129 A CN201610568129 A CN 201610568129A CN 106183309 A CN106183309 A CN 106183309A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- retardant
- flame
- electrostatic
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of feather dress fabric, it relates to down jackets technical field;It comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;It is provided with packed layer inside described inflaming retarding fabric outer layer, inside packed layer, is provided with fabric;Described inflaming retarding fabric outer layer is formed by 36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending;Composition and the content of described electrostatic flame-retardant yarn is: 40~48 mass parts flame-retardant acrylic fibres, 6~8 mass parts electrostatic fibres, 45~55 mass parts terylene, 20~25 mass parts fire-retardant nylons;Described inflaming retarding fabric outer layer inner surface pressing has ventilated membrane.A kind of feather dress fabric of the present invention, anti-flaming function is strong, and has stronger permeability, and winter worn safety by the down jackets made.
Description
Technical field
The present invention relates to down jackets technical field, be specifically related to a kind of feather dress fabric.
Background technology
Eider down is the most best natural material warming for the mankind, at the techniques such as washing, dry, classification
After reason, made down jackets by people.With artificial material is compared, the warming ability of eider down is three times of general artificial material.
High-grade down jackets typically select the white goose down of more than 90% or the white duck down of more than 90%, real more than 90%
Down jackets warmth retention property is strong, and loft is the highest, and down jackets dress is light again, the most comfortable.Generally use down content 90% eider down, fill floss amount
The down jackets of 230g ~ 320g just adapt to the environment at north minus 20 degrees ~ subzero about 30 degree.If down jackets hands is touched, as
It is absolutely not 90% eider down that fruit is touched if drawing a lot of hair bar, if down jackets hand pressure this then handle release, 90% plumage
Floss is the most fluffy replys original state, if the most then let go down jackets or flat appearance by hand pressure!
The possible down jackets that you buy are not reaching to 90% eider down, fill floss amount also not, and warmth retention property is the lowest.
Feather dress fabric kind, senior TC cloth, the down jackets sold in the market are mostly with nylon taffeta and TC cloth
Being main, general yarn count density is optimal at more than 230T, 250T, and below 230T is not then it is difficult to ensure that fine hair bores outward.
Down jackets in the market do not possess fire protecting performance, and owing to down jackets are more thick and heavy, winter, dry weather, ran into
Naked light, can light rapidly, brings on a disaster to the life of people, life, brings property loss simultaneously.
Summary of the invention
Present invention aims to defect and the deficiency of prior art, it is provided that a kind of down jackets with anti-flaming function
Fabric.
For achieving the above object, the technical solution used in the present invention is: it comprises inflaming retarding fabric outer layer, packed layer, comfortable
Endonexine;It is provided with packed layer inside described inflaming retarding fabric outer layer, inside packed layer, is provided with fabric;Described is fire-retardant
Fabric outer layer is formed by 36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending;Described electrostatic flame-retardant yarn
Composition and content be: 40~48 mass parts flame-retardant acrylic fibres, 6~8 mass parts electrostatic fibres, 45~55 mass parts terylene, 20~
25 mass parts fire-retardant nylons;Described inflaming retarding fabric outer layer inner surface pressing has ventilated membrane.
As preferably, composition and the content of described non-electrostatic flame-retardant yarn is: 25~30 mass parts fire-retardant nylons, 6~10
Mass parts terylene, 20~25 mass parts flame-retardant acrylic fibres.
As preferably, described ventilated membrane is polytetrafluoroethylene film.
What the present invention produced has the beneficial effect that a kind of feather dress fabric of the present invention, and anti-flaming function is strong, and has relatively
Strong permeability, winter worn safety by the down jackets made.
Detailed description of the invention
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, below will be to above-mentioned technical side
Case is described in detail.
Embodiment 1
A kind of feather dress fabric, adopts the following technical scheme that it comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;Described
Inflaming retarding fabric outer layer inside be provided with packed layer, be provided with fabric inside packed layer;Described inflaming retarding fabric outer layer by
36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending form;The composition of described electrostatic flame-retardant yarn and containing
Amount is: 40 mass parts flame-retardant acrylic fibres, 6 mass parts electrostatic fibres, 45 mass parts terylene, 20 mass parts fire-retardant nylons;Described resistance
Combustion fabric outer layer inner surface pressing has polytetrafluoroethylene film;Composition and the content of described non-electrostatic flame-retardant yarn is: 25 mass
Part fire-retardant nylon, 6 mass parts terylene, 20 mass parts flame-retardant acrylic fibres.
Embodiment 2
A kind of feather dress fabric, adopts the following technical scheme that it comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;Described
Inflaming retarding fabric outer layer inside be provided with packed layer, be provided with fabric inside packed layer;Described inflaming retarding fabric outer layer by
36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending form;The composition of described electrostatic flame-retardant yarn and containing
Amount is: 42 mass parts flame-retardant acrylic fibres, 7 mass parts electrostatic fibres, 48 mass parts terylene, 22 mass parts fire-retardant nylons;Described resistance
Combustion fabric outer layer inner surface pressing has polytetrafluoroethylene film;Composition and the content of described non-electrostatic flame-retardant yarn is: 27 mass
Part fire-retardant nylon, 7 mass parts terylene, 22 mass parts flame-retardant acrylic fibres.
Embodiment 3
A kind of feather dress fabric, adopts the following technical scheme that it comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;Described
Inflaming retarding fabric outer layer inside be provided with packed layer, be provided with fabric inside packed layer;Described inflaming retarding fabric outer layer by
36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending form;The composition of described electrostatic flame-retardant yarn and containing
Amount is: 45 mass parts flame-retardant acrylic fibres, 8 mass parts electrostatic fibres, 50 mass parts terylene, 23 mass parts fire-retardant nylons;Described resistance
Combustion fabric outer layer inner surface pressing has polytetrafluoroethylene film;Composition and the content of described non-electrostatic flame-retardant yarn is: 28 mass
Part fire-retardant nylon, 8 mass parts terylene, 23 mass parts flame-retardant acrylic fibres.
Embodiment 4
A kind of feather dress fabric, adopts the following technical scheme that it comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;Described
Inflaming retarding fabric outer layer inside be provided with packed layer, be provided with fabric inside packed layer;Described inflaming retarding fabric outer layer by
36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending form;The composition of described electrostatic flame-retardant yarn and containing
Amount is: 48 mass parts flame-retardant acrylic fibres, 8 mass parts electrostatic fibres, 55 mass parts terylene, 25 mass parts fire-retardant nylons;Described resistance
Combustion fabric outer layer inner surface pressing has polytetrafluoroethylene film;Composition and the content of described non-electrostatic flame-retardant yarn is: 30 mass
Part fire-retardant nylon, 10 mass parts terylene, 25 mass parts flame-retardant acrylic fibres.
A kind of feather dress fabric having the beneficial effect that described in this detailed description of the invention that this detailed description of the invention produces, resistance
Combustion function is strong, and has stronger permeability, and winter worn safety by the down jackets made.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The skill of the industry
The art personnel simply explanation it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description
The principle of the present invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these
Changes and improvements both fall within scope of the claimed invention.Claimed scope by appending claims and
Its equivalent defines.
Claims (3)
1. a feather dress fabric, it is characterised in that: it comprises inflaming retarding fabric outer layer, packed layer, comfortable endonexine;Described resistance
It is provided with packed layer inside combustion fabric outer layer, inside packed layer, is provided with fabric;Described inflaming retarding fabric outer layer by
36.6% non-electrostatic flame-retardant yarn and 63.4% electrostatic flame-retardant yarn blending form;The composition of described electrostatic flame-retardant yarn and containing
Amount is: 40~48 mass parts flame-retardant acrylic fibres, 6~8 mass parts electrostatic fibres, 45~55 mass parts terylene, 20~25 mass parts resistances
Combustion nylon;Described inflaming retarding fabric outer layer inner surface pressing has ventilated membrane.
A kind of feather dress fabric the most according to claim 1, it is characterised in that: the composition of described non-electrostatic flame-retardant yarn and
Content is: 25~30 mass parts fire-retardant nylons, 6~10 mass parts terylene, 20~25 mass parts flame-retardant acrylic fibres.
A kind of feather dress fabric the most according to claim 1, it is characterised in that: described ventilated membrane is that politef is thin
Film.