CN106078105A - A kind of production technology of aluminum alloy pattern plate - Google Patents
A kind of production technology of aluminum alloy pattern plate Download PDFInfo
- Publication number
- CN106078105A CN106078105A CN201610516063.1A CN201610516063A CN106078105A CN 106078105 A CN106078105 A CN 106078105A CN 201610516063 A CN201610516063 A CN 201610516063A CN 106078105 A CN106078105 A CN 106078105A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy pattern
- pattern plate
- sheet material
- aluminium profiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production technology of a kind of aluminum alloy pattern plate, belong to the technical field of producing of building pouring auxiliary mould, comprise the following steps: A, buying have the aluminium profiles sheet material of given shape；B, described aluminium profiles sheet material is carried out sawing sheet process；C, described aluminium profiles sheet material is carried out stamping process；D, described aluminium profiles sheet material is carried out soldering；E, described aluminum alloy pattern plate unit (1) is carried out grinding process；F, described aluminum alloy pattern plate unit (1) is carried out Shape correction, then carry out packing, process of dusting.Use such scheme in order to save offering of early stage mould, realized the demand of the aluminum alloy pattern plate of multiple types by later stage sawing sheet and welding.
Description
Technical field
The invention belongs to the technical field of producing of building pouring auxiliary mould, the production work of a kind of aluminum alloy pattern plate
Skill.
Background technology
Mould for building on current domestic market is substantially wood mold coupled, after this mould substantially uses once
Just thrown away when garbage, do not recycle, waste resource.
And the pouring face after wooden template split has substantial amounts of gap, the surface of wall after pouring can be caused to occur big
Measuring irregular striped, the further leveling process of these stripeds needs had both wasted resource and had wasted the time.Full aluminum alloy pattern plate
Technology has had the applicating history of 50 years in developed country.My company is carried out for integrated aluminum alloy pattern plate existing on market
Improve, save the cost offering various mould because aluminum alloy pattern plate is of a great variety.
Summary of the invention
The invention aims to save offering of early stage mould, realize multiple types by later stage sawing sheet and welding
The demand of aluminum alloy pattern plate.
The above-mentioned technical purpose of the present invention has the technical scheme that the production work of a kind of aluminum alloy pattern plate
Skill, it is characterised in that comprise the following steps:
A, buying have the aluminium profiles sheet material of given shape, and described aluminium profiles sheet material includes mainboard and is arranged on the company of described mainboard both sides
Fishplate bar, described mainboard forms groove with described connecting plate；It is provided with on described mainboard in described groove and is parallel to described company
The passage of fishplate bar；
B, described aluminium profiles sheet material is carried out sawing sheet process；Described aluminium profiles sheet material is intercepted suitable template size；And will be because intercepting
And remaining described aluminium profiles sheet material is placed on the most stand-by；
C, described aluminium profiles sheet material is carried out stamping process, on described connecting plate, offer connecting hole with pressing equipment；
D, described aluminium profiles sheet material is carried out soldering, by the described aluminium profiles sheet material intercepted by welding remaining described aluminium profiles plate
Material forms multiple aluminum alloy pattern plate unit；
E, described aluminum alloy pattern plate unit is carried out grinding process so that described aluminum alloy pattern plate cell surface is smooth；
F, described aluminum alloy pattern plate unit is carried out Shape correction, then carry out packing, process of dusting.
As preferably, in step A, described connecting plate is provided with the conduit of at least one parallel described mainboard.
As preferably, in step B, described template size includes the standard form that width is 400mm, and other width are respectively
Auxiliary template for 300mm, 250mm, 200mm, 150mm, 100mm, 50mm.
As preferably, in step D, multiple described aluminum alloy pattern plate unit include wall form, column template, beam forms, roof plate template,
Stair template, waft window template and profiled template.
As preferably, in described aluminum alloy pattern plate unit, it is welded with reinforcement connecting rod.
As preferably, remaining described aluminium profiles sheet material offers described connecting hole also by described pressing equipment.
In sum, the manufacture of aluminum alloy pattern plate have employed productive technology of short flow technology, the most well changes producing when
Enter the physical structural characteristic on aluminum alloy pattern plate surface.Early stage mold is made to form multiple aluminum dipping form by the sawing sheet in later stage and welding
The cost of plate decreases, because after offering the aluminum alloy pattern plate that a mould forms a structure, if the aluminum alloy pattern plate of this structure
Demand is not that the most whole very big mould just wastes, if so this mould that is in great demand also is easily damaged, needs
The most more mold exchange.So this technique of aluminum alloy pattern plate wanted by later stage sawing sheet and weld is simple and practical, will not
Waste resource, reduces cost.
Accompanying drawing explanation
Fig. 1 is the aluminum alloy pattern plate unit overall structure schematic diagram of the present invention；
Fig. 2 is the aluminum alloy pattern plate unit top view of the present invention；
In Fig. 1 and Fig. 2,1-aluminum alloy pattern plate unit, 11-mainboard, 12-connecting plate, 124-connecting hole, 125-conduit, 112a-passage,
112b-strengthens connecting rod.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention is described in further detail.
The production technology of aluminum alloy pattern plate unit 1 as depicted in figs. 1 and 2 is as follows:
The production technology of a kind of aluminum alloy pattern plate, comprises the following steps:
Buying has the aluminium profiles sheet material of given shape to be processed being formed the aluminum alloy pattern plate unit 1 of designated shape, and aluminum alloy pattern plate unit 1 includes
Mainboard 11 and connecting plate 12, mainboard 11 includes supporting surface and work surface, applicant buying when just choose supporting surface with
The aluminum alloy pattern plate unit 1 of two passage 112a, because the passage 112a on this sheet material and aluminum alloy pattern plate unit 1 Liancheng one,
It need not applicant's reprocessing, but also so that the structural strength change of whole aluminum alloy pattern plate unit 1 greatly will not be because of application
People is ensuing to be passed through the short production technology improved and deforms.The shape of aluminum alloy pattern plate unit 1 includes wall form, column template, beam form
Plate, roof plate template, stair template, waft window template and profiled template.The design drawing of the aluminium profiles sheet material of given shape is also to have this
Applicant provides, the drawing provided according to the applicant, and it is specific that the aluminum alloy smelting company corresponding Making mold of design goes out this
The aluminium profiles sheet material of shape.The cross section of passage 112a be one trapezoidal.
Aluminium profiles sheet material is by being processed by sawing sheet so that the aluminium profiles sheet material originally with uniform length is intercepted into each difference
Aluminum alloy pattern plate unit 1 blank of length；Aluminum alloy pattern plate unit 1 includes the standard form that width is 400mm, and other width are respectively
The auxiliary template of 300mm, 250mm, 200mm, 150mm, 100mm, 50mm.
Aluminium profiles sheet material after processing sawing sheet carries out stamping process so that offer some in the gripper shoe of aluminum alloy pattern plate unit 1
Facilitate the connecting hole 124 connected between aluminum alloy pattern plate unit 1, and be stamped and formed out conduit 125 at the dual-side of connecting hole 124.
Conduit 125 is can be to be stamped and formed out, it is also possible to just with this structure of conduit 125 when of buying.Because aluminium alloy
The when of molding in mould, mould just allows for arranging this structure of conduit with this structure of conduit and becomes relatively easy
A bit, although and the biggest by the channel structure difficulty that is stamped and formed out, but still it is achieved that so be two kinds different
Preferably.
Aluminium profiles sheet material after stamping process is carried out soldering so that be welded and fixed in aluminum alloy pattern plate unit 1 blank
Connection member and reinforcement connecting rod 112b, connection member is arranged on mainboard surrounding and is connected one entirety of formation with gripper shoe, connects
Parts are to be placed on the most stand-by remaining aluminium profiles sheet material, and connection member offers connecting hole 124 also by pressing equipment.
Strengthening connecting rod 112b and be welded on passage 112a surface, one is to be supported whole mainboard, and two is the most right
Passage 112a is supported；And strengthen connecting rod 112b be welded between connecting plate 12 and for cross section be one square
Hollow pipeline.
Aluminium profiles sheet material after soldering is carried out grinding process, and grinding process is to polish at above-mentioned welding understanding
And make the connection between connection member and mainboard and gripper shoe more smooth；First pass through operator and use grinding abrasive disk butt welding
The surrounding at the place of connecing polishes, and then grinding abrasive disk changes into frosted skin and polishes, since it is desired that ensure the every of aluminum alloy pattern plate unit
Square metre weight be 26-30kg.
Aluminium profiles sheet material after grinding process is carried out Shape correction, the aluminium profiles sheet material after Shape correction is carried out packing and dusts
Process forms aluminum alloy pattern plate unit 1.
Aluminum alloy pattern plate unit 1 after above-mentioned PROCESS FOR TREATMENT just can be transported to construction site and build the cavity of pouring
?.
This specific embodiment is only explanation of the invention, and it is not limitation of the present invention, people in the art
The present embodiment can be made after reading this specification by member as required does not has the amendment of creative contribution, but as long as at this
All protected by Patent Law in the right of invention.
Claims (6)
1. the production technology of an aluminum alloy pattern plate, it is characterised in that comprise the following steps:
A, buying have the aluminium profiles sheet material of given shape, and described aluminium profiles sheet material includes mainboard (11) and is arranged on described mainboard (11)
The connecting plate (12) of both sides, described mainboard (11) forms groove with described connecting plate (12)；Described mainboard in described groove
(11) passage (112a) being parallel to described connecting plate it is provided with on；
B, described aluminium profiles sheet material is carried out sawing sheet process；Described aluminium profiles sheet material is intercepted suitable template size；And will be because intercepting
And remaining described aluminium profiles sheet material is placed on the most stand-by；
C, described aluminium profiles sheet material is carried out stamping process, on described connecting plate (12), offer connecting hole (124) with pressing equipment；
D, described aluminium profiles sheet material is carried out soldering, by the described aluminium profiles sheet material intercepted by welding remaining described aluminium profiles plate
Material forms multiple aluminum alloy pattern plate unit (1)；
E, described aluminum alloy pattern plate unit (1) is carried out grinding process so that described aluminum alloy pattern plate unit (1) smooth surface is smooth；
F, described aluminum alloy pattern plate unit (1) is carried out Shape correction, then carry out packing, process of dusting.
The production technology of a kind of aluminum alloy pattern plate the most according to claim 1, it is characterised in that in step A, on described connecting plate
It is provided with the conduit (125) of at least one parallel described mainboard.
The production technology of a kind of aluminum alloy pattern plate the most according to claim 1, it is characterised in that in step B, described template size
It is the standard form of 400mm including width, and other width are respectively 300mm, 250mm, 200mm, 150mm, 100mm, 50mm
Auxiliary template.
The production technology of a kind of aluminum alloy pattern plate the most according to claim 1, it is characterised in that in step D, multiple described aluminum dipping form
Slab element (1) includes wall form, column template, beam forms, roof plate template, stair template, waft window template and profiled template.
5. according to the production technology of a kind of aluminum alloy pattern plate described in claim 1 or 4, it is characterised in that described aluminum alloy pattern plate unit (1)
Inside it is welded with reinforcement connecting rod (112b).
The production technology of a kind of aluminum alloy pattern plate the most according to claim 6, it is characterised in that on remaining described aluminium profiles sheet material
Described connecting hole (124) is offered also by described pressing equipment.