CN106007755A - Anchoring brick - Google Patents
Anchoring brick Download PDFInfo
- Publication number
- CN106007755A CN106007755A CN201610359005.2A CN201610359005A CN106007755A CN 106007755 A CN106007755 A CN 106007755A CN 201610359005 A CN201610359005 A CN 201610359005A CN 106007755 A CN106007755 A CN 106007755A
- Authority
- CN
- China
- Prior art keywords
- parts
- alumina
- weight
- powder
- particle material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anchoring brick. The anchoring brick comprises a main material and a bonding agent, wherein the main material comprises aggregates and power; the aggregates comprise the following components in parts by weight: 10 to 15 parts of 3 to 5mm alumina granules, 25 to 35 parts of 1 to 3mm alumina granules, 5 to 15 parts of 0 to 1mm alumina granules, and 5 to 15 parts of kyanite; the powder comprises the following components in parts by weight: 5 to 10 parts of combined clay powder, 15 to 25 parts of alumina pulverized clinker, and 15 to 25 parts of alumina raw powder; the bonding agent comprises the following components in parts by weight: 0.3 to 0.8 part of calcium lignosulphonate, and 0.1 to 0.3 part of yellow dextrin. The anchoring brick has the beneficial effects that the anchoring brick produced through the formula has higher refractoriness under load and thermal shock resistance capacity, and ensures that the service life of an industrial furnace is greatly prolonged.
Description
Technical field
The present invention relates to technical field of refractory materials, particularly to a kind of anchored brick.
Background technology
Compared with not burned product, amorphous refractory, the heat stability of burnt product is very poor, along with the technological progress of novel kiln, very strict to the thermal stability requirement of burnt product, has become the bottleneck of burnt product development for this heat stability.For anchored brick, in use play the fixing working lining of connection and heat-insulation layer as anchoring piece, at high temperature have to keep higher intensity.Additionally, its kiln used, in most cases, for service intermittent, repeatedly to stand variations in temperature in using, thus improve traditional processing technology, improve heat stability and the thermal shock resistance burning till anchored brick, can significantly extend the service life of anchored brick.Current industrial kiln blowing out overhaul is owing to anchoring piece therein fracture is caused mostly.Therefore highly heatproof and shockproof, high RUL anchored brick are developed the most necessary.
Summary of the invention
The purpose of the present invention is that and overcomes above-mentioned deficiency, it is provided that the anchored brick that a kind of heat stability is high, shock resistance is strong.
For reaching above-mentioned purpose, the present invention implements according to techniques below scheme:
A kind of anchored brick, including major ingredient and bonding agent, described major ingredient includes aggregate and powder, described aggregate is made up of the component of following parts by weight: alumina particle material 10-15 part of 3-5mm, alumina particle material 25-35 part of 1-3mm, alumina particle material 5-15 part of 0-1mm, kyanite 5-15 part of 0.5-1mm;Described powder is made up of the component of following parts by weight: bonding clay powder 5-10 part, bauxite clinker powder 15-25 part, Alumina fecula 15-25 part;Described bonding agent is made up of the component of following parts by weight: calcium lignosulfonate 0.3-0.8 part, yellow starch gum 0.1-0.3 part.
As the improvement to technique scheme, anchored brick is made up of the component of following parts by weight: 15 parts of 3-5mm alumina particle material, 30 parts of 1-3mm alumina particle material, 5 parts of 0-1mm alumina particle material, the kyanite of 0.5-1mm 10 parts, 5 parts of bonding clay powder, 20 parts of bauxite clinker powder, Alumina fecula 15 parts, calcium lignosulfonate 0.4 part, yellow starch gum 0.1 part.
Compared with prior art, the invention has the beneficial effects as follows: the anchored brick produced with this formula has stronger refractoriness under load and thermal shock resistance so that the life-span of industrial furnace is greatly improved.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described, and the illustrative examples invented at this and explanation are for explaining the present invention, but not as a limitation of the invention.
Embodiment 1
The component of anchored brick includes major ingredient and bonding agent, major ingredient includes aggregate and powder, and aggregate is made up of the component of following parts by weight: 10 parts of the alumina particle material of 3-5mm, 25 parts of the alumina particle material of 1-3mm, 10 parts of the alumina particle material of 0-1mm, the kyanite of 0.5-1mm 15 parts;Powder is made up of the component of following parts by weight: 5 parts of bonding clay powder, 15 parts of bauxite clinker powder, Alumina fecula 20 parts;Bonding agent is made up of the component of following parts by weight: calcium lignosulfonate 0.6 part, yellow starch gum 0.2 part.After pouring above-mentioned each component into blender, the clean water of additional 5%, after stirring, ageing mixture 2 hours is the most plastic.Adobe after molding i.e. can get finished product after being dried and the step such as burning till.
Embodiment 2
The component of anchored brick includes major ingredient and bonding agent, major ingredient includes aggregate and powder, and aggregate is made up of the component of following parts by weight: 15 parts of the alumina particle material of 3-5mm, 30 parts of the alumina particle material of 1-3mm, 5 parts of the alumina particle material of 0-1mm, the kyanite of 0.5-1mm 10 parts;Powder is made up of the component of following parts by weight: 5 parts of bonding clay powder, 20 parts of bauxite clinker powder, Alumina fecula 15 parts;Bonding agent is made up of the component of following parts by weight: calcium lignosulfonate 0.4 part, yellow starch gum 0.1 part.After pouring above-mentioned each component into blender, the clean water of additional 5%, after stirring, ageing mixture 2 hours is the most plastic.Adobe after molding i.e. can get finished product after being dried and the step such as burning till.
Embodiment 3
The component of anchored brick includes major ingredient and bonding agent, major ingredient includes aggregate and powder, and aggregate is made up of the component of following parts by weight: 10 parts of the alumina particle material of 3-5mm, 30 parts of the alumina particle material of 1-3mm, 10 parts of the alumina particle material of 0-1mm, the kyanite of 0.5-1mm 5 parts;Powder is made up of the component of following parts by weight: 10 parts of bonding clay powder, 15 parts of bauxite clinker powder, Alumina fecula 15 parts;Bonding agent is made up of the component of following parts by weight: calcium lignosulfonate 0.5 part, yellow starch gum 0.2 part.After pouring above-mentioned each component into blender, the clean water of additional 5%, after stirring, ageing mixture 2 hours is the most plastic.Adobe after molding i.e. can get finished product after being dried and the step such as burning till.
Technical scheme is not limited to the restriction of above-mentioned specific embodiment, and every technology deformation made according to technical scheme, within each falling within protection scope of the present invention.
Claims (2)
1. an anchored brick, it is characterized in that, including major ingredient and bonding agent, described major ingredient includes aggregate and powder, described aggregate is made up of the component of following parts by weight: alumina particle material 10-15 part of 3-5mm, alumina particle material 25-35 part of 1-3mm, alumina particle material 5-15 part of 0-1mm, kyanite 5-15 part of 0.5-1mm;Described powder is made up of the component of following parts by weight: bonding clay powder 5-10 part, bauxite clinker powder 15-25 part, Alumina fecula 15-25 part;Described bonding agent is made up of the component of following parts by weight: calcium lignosulfonate 0.3-0.8 part, yellow starch gum 0.1-0.3 part.
A kind of anchored brick the most according to claim 1, it is characterized in that, it is made up of the component of following parts by weight: 15 parts of 3-5mm alumina particle material, 30 parts of 1-3mm alumina particle material, 5 parts of 0-1mm alumina particle material, the kyanite of 0.5-1mm 10 parts, 5 parts of bonding clay powder, 20 parts of bauxite clinker powder, Alumina fecula 15 parts, calcium lignosulfonate 0.4 part, yellow starch gum 0.1 part.