CN105522727A - 光学超精密树脂镜片消应力工艺 - Google Patents

光学超精密树脂镜片消应力工艺 Download PDF

Info

Publication number
CN105522727A
CN105522727A CN201610044079.7A CN201610044079A CN105522727A CN 105522727 A CN105522727 A CN 105522727A CN 201610044079 A CN201610044079 A CN 201610044079A CN 105522727 A CN105522727 A CN 105522727A
Authority
CN
China
Prior art keywords
resin lens
lens
baking
ultraprecise
stress
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610044079.7A
Other languages
English (en)
Inventor
李雪高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Changyi Photoelectric Co Ltd
Original Assignee
Dongguan Changyi Photoelectric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Changyi Photoelectric Co Ltd filed Critical Dongguan Changyi Photoelectric Co Ltd
Priority to CN201610044079.7A priority Critical patent/CN105522727A/zh
Publication of CN105522727A publication Critical patent/CN105522727A/zh
Pending legal-status Critical Current

Abstract

本发明涉及镜片加工技术领域，尤其是指一种光学超精密树脂镜片消应力工艺，A、将树脂镜片放入清洗栏；B、将装有树脂镜片的清洗栏用耐高温保鲜膜包裹；C、将包裹后的清洗栏放入无尘烤箱内烘烤，烘烤时间是3～5小时，烘烤温度是75～95摄氏度；D、烘烤结束后自然冷却。本发明将树脂镜片在75～95摄氏度的温度下保温烘烤3～5小时，树脂分子重新组合，最大程度地消除了内应力，经组立后镜头在MTF下的检测结果显示光学树脂镜片内应力大幅减少，镜头解像良率得到较大提升，实用性较强。

Description

光学超精密树脂镜片消应力工艺
技术领域
本发明涉及镜片加工技术领域，尤其是指一种光学超精密树脂镜片消应力工艺。
背景技术
当前树脂镜片由于具有重量轻、透明度高、抗冲击、易成型、可染色等特点，在眼镜市场竞争中处于优先的地位。但是树脂材料结晶条件比较严格，在其注塑成型为镜片时，树脂往往为无定性结构，而且分子副性大，取向和解取自都比较困难，成型后的镜片内应力较大，另外在树脂镜片成型的过程中，当模具温度较底时，熔融物料进入模控后表面很快冷却凝自，而热的物料在压力的作用下，源源不断的进入模控，在冷料和热料间形成了较大的剪切应力，这些应力随熔体的冷却大部分被保留在了产品中，而且树脂熔钵在注塑过程中注塑过快则造成分子取向不一致，同样产生内应力，而如果速度较低就难以克服熔体流动阻力，使模腔内逐渐冷却的熔体缺少及时的补料而产生收缩，造成制品缺蹈，还会造成内应力。
但是光学镜片中存在内应力，会严重影嘀镜片的光学与机械性能，比如会使镜片产生双折射、镜片开裂等状况。自此树脂镜片在成型后，需要做内应力消除，才能出产销售与使用。
发明内容
本发明要解决的技术问题是提供一种有效消除内应力，且有效提高消除内应力产品合格率的光学超精密树脂镜片消应力工艺。
为了解决上述技术问题，本发明采用如下技术方案：
一种光学超精密树脂镜片消应力工艺，其特征在于包括如下步骤：
A、将树脂镜片放入清洗栏；
B、将装有树脂镜片的清洗栏用耐高温保鲜膜包裹；
C、将包裹后的清洗栏放入无尘烤箱内烘烤，烘烤时间是3～5小时，烘烤温度是75～95摄氏度；
D、烘烤结束后自然冷却。
其中，在步骤A中，先将所述树脂镜片装入镜片夹具内，再将镜片夹具连同树脂镜片一起放入所述清洗栏。
优选的，所述烘烤时间是3.8～4.3小时，烘烤温度是83～87摄氏度。
进一步优选的，所述烘烤时间是4.1小时，烘烤温度是86摄氏度。
其中，所述耐高温保鲜膜由聚甲基丙烯制成。
本发明的有益效果在于：
本发明提供了一种光学超精密树脂镜片消应力工艺，将树脂镜片在75～95摄氏度的温度下保温烘烤3～5小时，树脂分子重新组合，最大程度地消除了内应力，经组立后镜头在MTF下的检测结果显示光学树脂镜片内应力大幅减少，镜头解像良率得到较大提升，实用性较强。
附图说明
图1为本发明清洗栏的结构示意图。
图2为本发明镜片夹具的结构示意图。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例与附图对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
如图1和图2所示，一种光学超精密树脂镜片消应力工艺，包括如下步骤：
A、将树脂镜片放入清洗栏1；
B、将装有树脂镜片的清洗栏1用耐高温保鲜膜包裹；
C、将包裹后的清洗栏1放入无尘烤箱内烘烤，烘烤时间是3～5小时，烘烤温度是75～95摄氏度；
D、烘烤结束后自然冷却。
本实施例中，在步骤A中，先将所述树脂镜片装入镜片夹具2内，再将镜片夹具2连同树脂镜片一起放入所述清洗栏1，该镜片夹具2为可以批量盛装树脂镜片的镜片容器，其中设置有多个与镜片形状项对应的凹槽，便于提高树脂镜片的批量搬运和转移效率。
优选的实施方式是，所述烘烤时间是3.8～4.3小时，烘烤温度是83～87摄氏度，经组立后镜头在MTF下的检测结果显示光学树脂镜片内应力大幅减少，镜头解像良率得到较大提升。
最优选的实施方式是，所述烘烤时间是4.1小时，烘烤温度是86摄氏度，其中，所述耐高温保鲜膜由聚甲基丙烯制成，本实施例中，经组立后镜头在MTF下的检测结果显示光学树脂镜片内应力进一步大幅减少，镜头解像良率得到显著提升，内应力消除效果更加显著。
以上所述实施例仅表达了本发明的一种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。

Claims (5)

1.光学超精密树脂镜片消应力工艺，其特征在于包括如下步骤：
A、将树脂镜片放入清洗栏(1)；
B、将装有树脂镜片的清洗栏(1)用耐高温保鲜膜包裹；
C、将包裹后的清洗栏(1)放入无尘烤箱内烘烤，烘烤时间是3～5小时，烘烤温度是75～95摄氏度；
D、烘烤结束后自然冷却。
2.根据权利要求1所述的光学超精密树脂镜片消应力工艺，其特征在于：在步骤A中，先将所述树脂镜片装入镜片夹具(2)内，再将镜片夹具(2)连同树脂镜片一起放入所述清洗栏(1)。
3.根据权利要求1所述的光学超精密树脂镜片消应力工艺，其特征在于：所述烘烤时间是3.8～4.3小时，烘烤温度是83～87摄氏度。
4.根据权利要求1所述的光学超精密树脂镜片消应力工艺，其特征在于：所述烘烤时间是4.1小时，烘烤温度是86摄氏度。
5.根据权利要求1所述的光学超精密树脂镜片消应力工艺，其特征在于：所述耐高温保鲜膜由聚甲基丙烯制成。
CN201610044079.7A 2016-01-22 2016-01-22 光学超精密树脂镜片消应力工艺 Pending CN105522727A (zh)