CN104726004A - Semitransparent orange brown calcined sienna smell cleaning type polyurethane woodenware paint and preparation method thereof - Google Patents
Semitransparent orange brown calcined sienna smell cleaning type polyurethane woodenware paint and preparation method thereof Download PDFInfo
- Publication number
- CN104726004A CN104726004A CN201310700090.0A CN201310700090A CN104726004A CN 104726004 A CN104726004 A CN 104726004A CN 201310700090 A CN201310700090 A CN 201310700090A CN 104726004 A CN104726004 A CN 104726004A
- Authority
- CN
- China
- Prior art keywords
- clean taste
- agent
- type polyurethane
- semitransparent
- taste type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a semitransparent orange brown calcined sienna smell cleaning type polyurethane woodenware paint and a preparation method thereof. The paint comprises a component A and a component B according to a weight ratio of 1:0.5; the component A is composed of smell cleaning type alkyd resin, extinction powder, a dispersant, an orange brown color paste, a leveling agent, an antifoaming agent, an anti-settling agent and a solvent; and the component B is a non-benzene curing agent based on TDI and HDI trimer or adduct. The semitransparent orange brown calcined sienna smell cleaning type polyurethane woodenware paint prepared in the invention does not contain aromatic hydrocarbons, aldehyde, ketone or heavy metals, and can reach a smell cleaning effect 48h after a film is formed by coating the paint; the paint has the advantages of no settlement, good levelability, good handle, high scratch resistance and no ghosting in the storage process; and the paint can be coated on woodenware to realize clear and intensive wood grains and make furniture elegant, noble, natural and comfortable, adapts to modern aesthetics, is popular in the market and is loved by users. The paint can be widely used to realize surface decoration protection of woodenwares, metals and plastics.
Description
Technical field
The present invention relates to a kind of preparation method of bi-component polyurethane ester wood lacquer, particularly relate to a kind of semitransparent orange coffee calcined sienna clean taste type scratch resistance two component polyurethane lacquer as woodenware finish.
Background technology
Along with the raising of people's material and cultural life, human consumer requires also more and more higher to the painting effect of furniture, thus has driven the quick growth of domestic woodwork coating.On furniture Coating Market, American and European style furniture occupies the larger market share, domestic furniture industry all uses look essence (a kind of metallized dye mostly, there is such as heavy metal severe overweight, poor containing morbid substance, temperature tolerance, light permanency, resistance to migration in this type of dyestuff, be commonly called as Ge Lisi) carry out wood grain wiping look and Lacquer finish colouring matter, the resin wiping look is mostly common Synolac and oleum lini, and after application, interior furniture still has peculiar smell for a long time; The requirement of wood lacquer market to painting huge is now more and more higher, dragon its be that woodenware urethane (PU) paints excellent combination property, human consumer uses extensively, but product exists many weak points, and as turned white, bubbling, delamination, not scratch resistance, ghost, impression of the hand not easily disappear.
Semitransparent orange coffee calcined sienna powder pigment has excellent weathering resistance, photostabilization, ultraviolet-absorbing, transparency is high, color is elegant, nontoxic, excellent chemical stability, excellent alkaline-resisting, acid resistance.Translucent forging raw received toner to have good temperature tolerance is 300 DEG C; And raw forging rawly receives toner without bleeding, resistance toly to migrate with insoluble.
Ultraviolet destroys wooden arch-criminal, and forge raw toner pigment energy strong absorption ultraviolet radiation of receiving, thus protect wooden, and make Wood Energy play coloring effect, and can make again wooden maintenance native texture, color is soft; And translucent forge raw receive toner pigment and organic transparent pigment used in combination time, not only can enrich the color of pigment, improve chroma, and the deficiency of usual weathering resistance when organic transparent pigment is used alone, temperature tolerance difference can be improved significantly, make wood grain thoroughly clear time painted for wood furniture, furniture is seemed, and elegance is noble, natural and unaffected.
In suite room furniture field of coating, a difficult problem of puzzlement industry is that furniture is delivered to when installing in terminal client man and reflected that smell is large, and pungent unpleasant, many customer requirements are returned goods or exchanged goods.In the coating process of furniture, after the abnormal and application of the smell of working-yard, furniture smell is two kinds of different states.The former be different workmen to the sensitivity of different organic solvents because different personnel cause working-yard smell to be complained to the odor type of different solvents and irritating smell sensory difference, this just can be dealt with problems by the different thinner of apolegamy; The latter is uncomfortable property smell the having the greatest impact to client that after application, dried coating film is residual after 48 hours, therefore develops the demand that a kind of American Style Furniture meets client with clean taste type scratch-resistant polyurethane woodenware Lacquer finish finish paint necessary.
Summary of the invention
The present invention selects the clean taste type scratch resistance Synolac of hydroxyl value > 120mgKOH/g, this resin contains rigid molecular structure, have that scratch resistance, hardness are high, the feature such as quick-drying, wear-resisting, color inhibition, containing more primary hydroxyl in resin structure, sterically hindered little, be conducive to being cross-linked into reticulated structure with NCO in solidifying agent, improve film performance; And second-order transition temperature is high, be conducive to solvent release, accelerate the convection current of film internal solvent and the increase of top layer viscosity, the release of accelerated solvent; Cause flatting silica to be detained more, consumption is few simultaneously, and eliminate optical property is good, good leveling property, thus the gloss of raising film, transparency, fullness ratio and anti-scratch performance; And this resin containing vegetables oil (lipid acid), without benzene without ketone, therefore toxicity is low, the wood lacquer made coating, drying after 48 hours film reach clean taste effect.
Modified siloxane type defoamer selected by defoamer of the present invention, effectively can eliminate bubble and can not produce again surface atomizing and shrinkage cavity phenomenon.
The present invention selects chelate modified flow agent or silicon-oxygen polymer flow agent, unstable bubble, can provide excellent levelling property again can froth breaking.Due to the special role of titanic acid ester group, greatly improve the long wave levelling of paint film, eliminate dry rear appearance " large wave " phenomenon of paint film, make paint film reach mirror effect.Because titanic acid ester has close organic phase, close inorganic phase specific groups, can wets out pigments and ground quickly and effectively, improve wettability, the defoaming of paint film, thus make paint film have excellent planeness and dry after not easily produce advantages such as sinking.And silicon-oxygen polymer flow agent, can reduce the surface tension of paint film, antiskid is felt well good hand touch, improves resistance to marring, does not affect recoatability and ply adhesion, without ghost.
In order to solve technical problem recited above, the present invention takes following technical scheme: the present invention relates to a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer, be made up of resin paint first component and solidifying agent second component, the weight proportion of the first and second components is 1:0.5; Described resin paint first component comprises clean taste type scratch resistance Synolac 40% ~ 60%, flatting silica 0% ~ 6%, dispersion agent 0.1% ~ 1%, orange coffee-like mill base 3% ~ 30%, modification flow agent 0.1% ~ 0.5%, defoamer 0.1% ~ 0.5%, anti-settling agent 0.2% ~ 3% and solvent 5% ~ 20%; Described solidifying agent second component comprises TDI-HDI mixed trimer or TDI/TMP affixture 30 ~ 40%, HDI tripolymer 25 ~ 35% and solvent 25 ~ 35%.
Wherein, Synolac selects the clean taste type scratch resistance Synolac of hydroxyl value >=120mgKOH/g, acid number < 10mgKOH/g.
The solvent-borne type semitransparent orange coffee calcined sienna mill base of fineness≤5 μ selected by the coffee-like mill base of orange.
Flatting silica selects the one of silicon-dioxide through Lasaxing Oilfield and organic wax powder.
Dispersion agent selects the copolymer dispersant of modified block structure.
Modification flow agent selects one or its combination of titanic acid ester modified organic silicon flow agent, titanic acid ester modified polyacrylate flow agent, organosilicon-modified acrylic flow agent, fluorin modified crylic acid flow agent, silicon-oxygen polymer flow agent.
Defoamer selects one or its combination of modified siloxane defoamer, polyacrylic ester defoamer.
Anti-settling agent select through dimethyldichlorosilane(DMCS) surface-treated hydrophobic type fumed silica [, the one of modified urea polymkeric substance, polyamide wax.
Solvent selects N-BUTYL ACETATE, vinyl acetic monomer, 2-butyl acetate, dimethyl cyclohexane, PMA, DBE, HDBE, the one of hydrogenation dearomatization D40 solvent or its combination.
The coffee-like mill base of orange of the present invention comprises semitransparent orange coffee calcined sienna powder 10 ~ 30%, clean taste type scratch resistance Synolac 30 ~ 55%, mill base dispersion agent 3 ~ 15%, defoamer 0.2 ~ 0.5%, anti-settling agent 0.2 ~ 2% and solvent 10 ~ 40%.
Mill base dispersion agent is selected containing derivative of fatty acid high molecular polymer, amino-contained derivative poly carboxylic acid high molecular polymer, polyphosphazene polymer ether compound containing pigment affinity groups, as one or its combination of EFKA-4310, EFKA-4010, DISPERBYK-110, DISPERBYK-180, DISPERBYK-183, DISPERBYK-2050, TEGO-610, TEGO-610S, TEGO-630, TEGO-655.
The present invention proposes the preparation method of the orange coffee-like mill base of a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer, its preparation technology is as follows: add mixed solvent by formulation weight than in dispersion bucket, clean taste type scratch resistance Synolac, mill base dispersion agent stirs, slowly add semitransparent orange coffee calcined sienna powder, then at the high shear 45 ~ 60min of 1000 ~ 1200r/min, arrive sand mill circular grinding again 4 ~ 6 times, until the fineness particle diameter of mill base reaches requirement≤5 μ, moving on to paint mixing bucket froth breaking adjusts sticky, filter and package obtained orange coffee-like mill base.
The present invention proposes the preparation method of a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer, its preparation technology is as follows: by formulation weight ratio, partial solvent is added in dispersion bucket, add clean taste type scratch resistance Synolac, mixed solvent stirring and dissolving is even, require to add flatting silica according to gloss, dispersion agent, high speed dispersion 30 ~ 40min, orange coffee-like mill base is added under stirring at low speed, flow agent, defoamer, anti-settling agent, solvent, the good viscosity of stirring and adjusting, filter and package i.e. obtained a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer.
The semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer aromatic free that the present invention obtains, containing aldehyde ketone, not containing heavy metal, coating film forming reaches clean taste effect after 48 hours, be a kind of environmental protection clean taste type polyurethane wood lacquer; And do not precipitate when storing, good leveling property, good hand touch, scratch resistance is high, without ghost; It is thoroughly clear that painting installs to wood grain on woodenware, furniture seemed and to the sensation that a kind of gracefulness of people is comfortable, adapts to modern Aesthetic View, very by the favor in market and liking of client by elegant noble, natural and unaffected.Be widely used in the surface decoration protections such as woodenware, metal, plastics to use.
Embodiment
Embodiment 1:
22.5 parts of mixed solvents are added than in dispersion bucket by formulation weight, add the 70% clean taste Synolac 50 parts admittedly contained, add DISPERBYK-110 mill base dispersion agent 7 parts to stir, slowly add 20 parts of semitransparent orange coffee calcined sienna powder, defoamer 0.2 part, anti-settling agent 0.3 part, then at the high shear 45 ~ 60min of 800 ~ 1000r/min, move on to horizontal sand mill circular grinding 5 ~ 8 times, until the fineness particle diameter of mill base reaches requirement≤5 μ, moving on to paint mixing bucket froth breaking adjusts sticky, filters and packages and obtains orange coffee-like mill base.
Embodiment 2:
Mixed solvent 22.8 parts is added than in dispersion bucket by formulation weight, add the 70% clean taste Synolac 55 parts admittedly contained, stir, add flatting silica 5 parts, dispersion agent 0.5 part, high speed dispersion 30 ~ 40min, under stirring at low speed, add orange coffee-like mill base 15 parts, the organosilicon chelating flow agent 0.3 part of titanic acid ester modification, fluorin modified crylic acid flow agent 0.2 part, modified siloxane defoamer 0.2 part, anti-settling agent 1 part, stir qualified after testing after filter and package i.e. obtained semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer first component.
Embodiment 3:
In dispersion bucket, add TDI/TMP affixture 40 parts, HDI tripolymer 30 parts, mixed solvent 30 parts stir, after qualified after testing, filter and package i.e. obtained semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer second component.
According to first component: second component=1:0.5 proportioning paint, add thinner and be transferred to the viscosity that can spray or brush.
According to relevant national standard, detect the performance of the semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer that the present invention obtains, test result is as shown in table 1.
Table 1 semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer the performance test results
Test event | Test result |
Paint film appearance | 5 light splitting, transparent, orange coffee color |
Surface drying | 23min |
Do solid work | 24h |
Pencil hardness | 2H |
Sticking power | 1 grade |
Snappiness | 2mm |
Gloss | 52~56% |
Fullness ratio | Good |
Feel | Good |
Levelling property | Excellent |
Scratch resistant | Good |
Recoatability | Good |
Triphen burst size 1. | ≤1.6mg/m 3 |
TVOC burst size 2. | ≤15mg/m 3 |
Free aldehyde burst size 3. | ≤0.2mg/m 3 |
Heavy metal content | ND |
TDI, HDI content summation | ≤0.4% |
Fatty acid content | ≤1.0% |
Halohydrocarbon content | ≤0.1% |
Film smell | Odorlessness after 48h |
Note: 1. ~ be 3. paint film test plate (panel) dry 48h in normal conditions behind spraying two road, be discharged into harmful substance contents measured in air by the method test paint film of regulation.
Although the present invention has been explained in detail and has quoted embodiment as proof, for those of ordinary skill in the art, the various schemes obviously can made according to above-mentioned explanation, amendment and change, within the scope that all should be included in claim.
Claims (10)
1. a semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer, is characterized in that: be made up of resin paint first component and solidifying agent second component, and the weight proportion of the first and second components is 1:0.5; Described resin paint first component comprises clean taste type scratch resistance Synolac 40% ~ 60%, flatting silica 0% ~ 6%, dispersion agent 0.1% ~ 1%, orange coffee-like mill base 3% ~ 30%, modification flow agent 0.1% ~ 0.5%, defoamer 0.1% ~ 0.5%, anti-settling agent 0.2% ~ 3% and solvent 5% ~ 20%; Described solidifying agent second component comprises TDI-HDI mixed trimer or TDI/TMP affixture 30 ~ 40%, HDI tripolymer 25 ~ 35% and solvent 25 ~ 35%.
2. a kind of semitransparent orange coffee calcined sienna as claimed in claim 1 clean taste type polyurethane wood lacquer, is characterized in that: described flatting silica selects the one of silicon-dioxide through Lasaxing Oilfield and organic wax powder.
3. a kind of semitransparent orange coffee calcined sienna as claimed in claim 1 clean taste type polyurethane wood lacquer, is characterized in that: the coffee-like mill base of described orange selects the solvent-borne type semitransparent orange coffee calcined sienna pink colour of fineness≤5 μ to starch; Comprise semitransparent orange coffee calcined sienna powder 10 ~ 30%, clean taste type scratch resistance Synolac 30 ~ 55%, mill base dispersion agent 3 ~ 15%, defoamer 0.2 ~ 0.5%, anti-settling agent 0.2 ~ 2% and solvent 10 ~ 40%.
4. a kind of semitransparent orange coffee calcined sienna as claimed in claim 1 clean taste type polyurethane wood lacquer, is characterized in that: described modification flow agent selects one or its combination of titanic acid ester modified organic silicon flow agent, titanic acid ester modified polyacrylate flow agent, organosilicon-modified acrylic flow agent, fluorin modified crylic acid flow agent, silicon-oxygen polymer flow agent.
5. a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer as described in claim 1,3, is characterized in that: described defoamer selects one or its combination of modified siloxane defoamer, polyacrylic ester defoamer.
6. a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer as described in claim 1,3, is characterized in that: the one through dimethyldichlorosilane(DMCS) surface-treated hydrophobic type fumed silica, modified urea polymkeric substance, polyamide wax selected by described anti-settling agent.
7. a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer as described in claim 1,3, is characterized in that: described solvent selects N-BUTYL ACETATE, vinyl acetic monomer, 2-butyl acetate, dimethyl cyclohexane, PMA, DBE, HDBE, the one of hydrogenation dearomatization D40 solvent or its combination.
8. a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer as described in claim 1,3, it is characterized in that: described mill base dispersion agent is selected containing derivative of fatty acid high molecular polymer, amino-contained derivative poly carboxylic acid high molecular polymer, polyphosphazene polymer ether compound containing pigment affinity groups, as one or its combination of EFKA-4310, EFKA-4010, DISPERBYK-110, DISPERBYK-180, DISPERBYK-183, DISPERBYK-2050, TEGO-610, TEGO-610S, TEGO-630, TEGO-655.
9. as claim 1, a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer described in 3 preparation method of orange coffee-like mill base, it is characterized in that: add mixed solvent by formulation weight than in dispersion bucket, clean taste type scratch resistance Synolac, mill base dispersion agent stirs, slowly add semitransparent orange coffee calcined sienna powder, then at the high shear 45 ~ 60min of 1000 ~ 1200r/min, arrive sand mill circular grinding again 4 ~ 6 times, until the fineness particle diameter of mill base reaches requirement≤5 μ, moving on to paint mixing bucket froth breaking adjusts sticky, filter and package obtained orange coffee-like mill base.
10. the preparation method of a kind of semitransparent orange coffee calcined sienna as claimed in claim 1 clean taste type polyurethane wood lacquer, it is characterized in that: by formulation weight ratio, partial solvent is added in dispersion bucket, add clean taste type scratch resistance Synolac, mixed solvent stirring and dissolving is even, require to add flatting silica according to gloss, dispersion agent, high speed dispersion 30 ~ 40min, orange coffee-like mill base is added under stirring at low speed, flow agent, defoamer, anti-settling agent, solvent, the good viscosity of stirring and adjusting, filter and package i.e. obtained a kind of semitransparent orange coffee calcined sienna clean taste type polyurethane wood lacquer.