CN104388886A - Process for remanufacturing corrugator roll - Google Patents
Process for remanufacturing corrugator roll Download PDFInfo
- Publication number
- CN104388886A CN104388886A CN201410606221.3A CN201410606221A CN104388886A CN 104388886 A CN104388886 A CN 104388886A CN 201410606221 A CN201410606221 A CN 201410606221A CN 104388886 A CN104388886 A CN 104388886A
- Authority
- CN
- China
- Prior art keywords
- corrugator roller
- coating
- less
- manufacturing process
- process again
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a process for remanufacturing a corrugator roll. The process comprises the following steps: (1) early treatment: (a) degreasing and removing oil; (b) removing rust; (c) phosphorizing; (d) blasting sand; (2) spraying: spraying an Ni-Cu-W coating by adopting high velocity oxygen fuel spraying equipment; (3) post-treatment, namely polishing by a fiber grinding wheel. By adopting the Ni-Cu-W coating, the microscopic tissues of the coating on the surface of a material can be improved, the abrasion resistance of the material surface can be integrally improved, and the process has a remarkable effect of enhancing the corrective comprehensive mechanical performance; cubic boron nitride is a hard material second to diamond, has excellent physical and chemical properties, the hardness and abrasion resistance of the surface of the corrugator roll can be greatly improved by adopting a cubic boron nitride auxiliary, so that the service life of the corrugator roll can be prolonged and the maintenance cost can be reduced.
Description
Technical field
The present invention relates to re-manufacturing technology field, specifically a kind of Corrugator roller manufacturing process again.
Background technology
Corrugator roller is most important integral part in corrugated board production device, and it generally all adopts 48CrMoA steel, and through medium frequency quenching or nitriding treatment, its hardness is general all at more than HRC55.Corrugator roller is the important vital part of single-side machine.Corrugator roller is divided into upper corrugated roller and lower corrugated roller, and upper and lower roll surface is female shape, and two roller mating engagement assemblings, its meshing mechanism is different from common geartransmission.Lower corrugated roller is drive roll, and axle head is equipped with gear, and electric motor drives lower corrugated roller to rotate through deceleration device.Upper corrugated roller is driven roll, relies on the roller tooth of top roll and the roller tooth of lower roll to engage each other transmission.May be there are some defects in Corrugator roller, such as pit etc. after use after a while, if Corrugator roller occurs these defects, will likely cause manufactured quality of corrugated low, but also likely cause Corrugator roller to use.If scrapped for some defective Corrugator rollers, very large waste will be caused, so manufacture extremely important again to the reparation of defective Corrugator roller, the work-ing life of Corrugator roller can not only be extended like this, and can also maintenance cost be reduced.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of Corrugator roller manufacturing process again.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of Corrugator roller manufacturing process again, comprises following processing step:
(1) process in early stage:
A) degreasing, oil removing;
B) eliminate rust; The rust on removing Corrugator roller surface;
C) phosphatization; Corrugator roller can be prevented after phosphatization to be corroded, also can to improve the coating of spraying and the sticking power of Corrugator roller;
D) sandblasting;
(2) spray: adopt supersonic velocity flame plating equipment spraying Ni-Cu-W coating;
(3) post-processed: fiber grinding wheel polished finish.
Spray parameters in described step (2) is: frock rotating speed is 240r/min; Flame distance is 15cm; Powder sending quantity control voltage is 5v, and flame temperature is 2000 DEG C, and spray gun translational speed is 0.01m/s;
Gas flow: air is 120L/H, oxygen is 30L/H, and propane is 25L/H;
Equipment gaseous tension: propane pressure is not less than 0.5MPa; Oxygen pressure is not less than 0.4MPa; Air pressure is not less than 0.6MPa; Hydrogen pressure is not less than 0.1MPa; Nitrogen pressure is not less than 0.2MPa.
The Ni-Cu-W coating of spraying comprises following component in described step (2): Ni is 23%, Cu be 33%, W is 41.75%, and trace element is 0.25%, and auxiliary agent is 2%.
Described auxiliary agent is CBN.
Described trace element comprises Si, B, Co.
The invention has the beneficial effects as follows: the present invention adopts Ni-Cu-W coating, improve the microtexture of material surface coating, thus the overall wear resisting property improving material surface, also there is significant effect to the comprehensive mechanical property improving improvement simultaneously, cubic boron nitride is only second to adamantine second hard material, there is good physics, chemical property, cubic boron nitride is adopted to substantially increase hardness and the wear resistance on Corrugator roller surface as auxiliary agent, thus extend the work-ing life of Corrugator roller, reduce maintenance cost.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below the present invention being set forth further.
Embodiment one:
A kind of Corrugator roller manufacturing process again, comprises following processing step:
(1) process in early stage:
A) degreasing, oil removing;
B) eliminate rust; The rust on removing Corrugator roller surface;
C) phosphatization; Corrugator roller can be prevented after phosphatization to be corroded, also can to improve the coating of spraying and the sticking power of Corrugator roller;
D) sandblasting;
(2) spray: adopt supersonic velocity flame plating equipment spraying Ni-Cu-W coating;
Spray parameters in described step (2) is: frock rotating speed is 240r/min; Flame distance is 15cm; Powder sending quantity control voltage is 5v, and flame temperature is 2000 DEG C, and spray gun translational speed is 0.01m/s;
Gas flow: air is 120L/H, oxygen is 30L/H, and propane is 25L/H;
Equipment gaseous tension: propane pressure is not less than 0.5MPa; Oxygen pressure is not less than 0.4MPa; Air pressure is not less than 0.6MPa; Hydrogen pressure is not less than 0.1MPa; Nitrogen pressure is not less than 0.2MPa.
The Ni-Cu-W coating of spraying comprises following component in described step (2): Ni is 23%, Cu be 33%, W is 41.75%, and trace element is 0.25%, and auxiliary agent is 2%.
Described auxiliary agent is CBN.
Described trace element comprises Si, B, Co.
(3) post-processed: fiber grinding wheel polished finish.
In order to prove actual effect of the present invention, the Corrugator roller after spy implements embodiment one by experiment detects, and the data of detected result are as follows:
Hardness (HRC) | Coating density (g/cm 3) | Coat-thickness (mm) |
63 | 8.96 | 3 |
From above-mentioned experimental data, the hardness being sprayed on the coating on Corrugator roller reaches HRC63, and coat-thickness can reach 3 millimeters, and the bonding strength of coating is better, and the density of tissue is better, and coating density can reach 8.96g/cm
3.
As can be seen here, after adopting the present invention, the performance of Corrugator roller can be improved greatly, realize manufacture again and the use of Corrugator roller, reduce the cost of the manufacturing, also extend the work-ing life of Corrugator roller.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not by the restriction of step embodiment; the just principle of the present invention described in step embodiment and specification sheets; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. a Corrugator roller manufacturing process again, is characterized in that: comprise following processing step:
(1) process in early stage:
A) degreasing, oil removing;
B) eliminate rust;
C) phosphatization;
D) sandblasting;
(2) spray: adopt supersonic velocity flame plating equipment spraying Ni-Cu-W coating;
(3) post-processed: fiber grinding wheel polished finish.
2. a kind of Corrugator roller according to claim 1 manufacturing process again, is characterized in that: the spray parameters in described step (2) is: frock rotating speed is 240r/min; Flame distance is 15cm; Powder sending quantity control voltage is 5v, and flame temperature is 2000 DEG C, and spray gun translational speed is 0.01m/s;
Gas flow: air is 120L/H, oxygen is 30L/H, and propane is 25L/H;
Equipment gaseous tension: propane pressure is not less than 0.5MPa; Oxygen pressure is not less than 0.4MPa; Air pressure is not less than 0.6MPa; Hydrogen pressure is not less than 0.1MPa; Nitrogen pressure is not less than 0.2MPa.
3. a kind of Corrugator roller according to claim 1 manufacturing process again, it is characterized in that: the Ni-Cu-W coating of spraying comprises following component in described step (2): Ni is 23%, Cu be 33%, W is 41.75%, trace element is 0.25%, and auxiliary agent is 2%.
4. a kind of Corrugator roller according to claim 3 manufacturing process again, is characterized in that: described auxiliary agent is CBN.
5. a kind of Corrugator roller according to claim 3 manufacturing process again, is characterized in that: described trace element comprises Si, B, Co.