CN104178152A - Dysprosium-doped alkali tantalate up-conversion luminescent material and preparation method and application thereof - Google Patents
Dysprosium-doped alkali tantalate up-conversion luminescent material and preparation method and application thereof Download PDFInfo
- Publication number
- CN104178152A CN104178152A CN201310196471.XA CN201310196471A CN104178152A CN 104178152 A CN104178152 A CN 104178152A CN 201310196471 A CN201310196471 A CN 201310196471A CN 104178152 A CN104178152 A CN 104178152A
- Authority
- CN
- China
- Prior art keywords
- dysprosium
- luminescent material
- conversion luminescent
- alkali
- doped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A dysprosium-doped alkali tantalate up-conversion luminescent material has the following chemical general formula of MeTa1-xO3:xDy<3+>,wherein x is 0.01-0.08, and Me is one of lithium, sodium, potassium, rubidium and cesium elements. In a photoluminescence spectrum of the dysprosium-doped alkali tantalate up-conversion luminescent material, the excitation wavelength of the dysprosium-doped alkali tantalate up-conversion luminescent material is 796 nm, the luminescence peak at 483 nm is transition radiation luminescence from <4>F9/2 to <6>F15/2 of Dy<3+>, and the dysprosium-doped alkali tantalate up-conversion luminescent material can be used as a blue light luminescent material. The invention also provides a preparation method of the dysprosium-doped alkali tantalate up-conversion luminescent material, and organic light-emitting diodes using the dysprosium-doped alkali tantalate up-conversion luminescent material.
Description
Technical field
The present invention relates to a kind of dysprosium alkali-doped tantalate up-conversion luminescent material, preparation method and Organic Light Emitting Diode.
Background technology
Organic Light Emitting Diode (OLED) because unit construction is simple, the characteristic such as cheap, the luminous of production cost, reaction times be short, flexible, and obtained the utmost point, apply widely.But owing to obtaining at present, the OLED blue light material of stability and high efficiency is more difficult, has limited greatly the development of white light OLED device and light source industry.
Upconverting fluorescent material can be launched visible ray under long wave (as infrared) radiation excitation, even UV-light, is with a wide range of applications in fields such as optical fiber communication technology, fibre amplifier, 3 D stereo demonstration, biomolecules fluorescence labelling, infrared detectives.But, can be by infrared, the long-wave radiations such as red-green glow inspire the dysprosium alkali-doped tantalate up-conversion luminescent material of blue emission, have not yet to see report.
Summary of the invention
Based on this, being necessary to provide a kind of can be inspired dysprosium alkali-doped tantalate up-conversion luminescent material, the preparation method of blue light and be used the Organic Light Emitting Diode of this dysprosium alkali-doped tantalate up-conversion luminescent material by long-wave radiation.
A dysprosium alkali-doped tantalate up-conversion luminescent material, has following chemical formula MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
Described x is 0.04.
A preparation method for dysprosium alkali-doped tantalate up-conversion luminescent material, comprises the following steps: according to MeTa
1-xo
3: xDy
3+the stoichiometric ratio of each element takes Me
2o, Ta
2o
5and Dy
2o
3powder, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element;
The powder taking is mixed to be dissolved in and in acidic solution, carry out crystallization treatment and obtain crystallisate;
Crystallisate is dissolved in solvent, then add ammoniacal liquor to regulate pH value to be 1~6, to obtain mixing solutions;
Described mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 150 ℃~500 ℃, be incubated 2 hours~10 hours, be precipitated thing, after being adopted to washings washing, the throw out obtaining is dried, then by dried throw out 800 ℃~1000 ℃ calcinations 0.5 hour~5 hours, obtaining chemical general formula is MeTa
1-xo
3: xDy
3+dysprosium alkali-doped tantalate up-conversion luminescent material.
Described x is 0.04.
Described mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 300 ℃, is incubated 3 hours.
Described crystallisate is dissolved in solvent, wherein said solvent is the mixing solutions of distilled water or distilled water and dehydrated alcohol.
Described acidic solution is nitric acid, sulfuric acid or hydrochloric acid.
Described pH value is 5.
Described washings is distilled water and dehydrated alcohol.
A kind of Organic Light Emitting Diode, comprise the substrate, negative electrode, organic luminous layer, anode and the transparent encapsulated layer that stack gradually, in described transparent encapsulated layer, doped with dysprosium alkali-doped tantalate up-conversion luminescent material, the chemical formula of this dysprosium alkali-doped tantalate up-conversion luminescent material is MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
Hydrothermal method mild condition, the synthesis temperature of above-mentioned dysprosium alkali-doped tantalate up-conversion luminescent material are low more easy to control, and granularity and the pattern of product are controlled, the powder complete crystallization of preparation, good dispersity, cost is lower, produces comparatively environmental protection in simultaneous reactions process without the three wastes; In the photoluminescence spectra of the dysprosium alkali-doped tantalate up-conversion luminescent material of preparation, the excitation wavelength of dysprosium alkali-doped tantalate up-conversion luminescent material is 796nm, and the glow peak of the 482nm obtaining, is Dy
3+ion
4f
9/2→
6f
15/2transition radiation luminous, can be used as blue light emitting material.
Accompanying drawing explanation
Fig. 1 is the structural representation of the Organic Light Emitting Diode of an embodiment.
Fig. 2 is the photoluminescence spectrogram of the dysprosium alkali-doped tantalate up-conversion luminescent material of embodiment 1 preparation.
Fig. 3 is the XRD spectra of the dysprosium alkali-doped tantalate up-conversion luminescent material of embodiment 1 preparation.
Fig. 4 is the spectrogram of the Organic Light Emitting Diode that forms doped with dysprosium alkali-doped tantalate up-conversion luminescent material in the transparent encapsulated layer of embodiment 1 preparation.
Embodiment
Below in conjunction with the drawings and specific embodiments, dysprosium alkali-doped tantalate up-conversion luminescent material and preparation method thereof is further illustrated.
The dysprosium alkali-doped tantalate up-conversion luminescent material of one embodiment, its chemical formula is MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
Preferably, x is 0.04.
In the photoluminescence spectra of this dysprosium alkali-doped tantalate up-conversion luminescent material, the excitation wavelength of dysprosium alkali-doped tantalate up-conversion luminescent material is 796nm, and the glow peak of the 482nm obtaining, is Dy
3+ion
4f
9/2→
6f
15/2transition radiation luminous, can be used as blue light emitting material.
The preparation method of above-mentioned dysprosium alkali-doped tantalate up-conversion luminescent material, comprises the following steps:
Step S11, according to MeTa
1-xo
3: xDy
3+the stoichiometric ratio of each element takes Me
2o, Ta
2o
5and Dy
2o
3powder, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
In this step, preferred, x is 0.04.
In this step, preferred, Me
2o, Ta
2o
5and Dy
2o
3the mol ratio of powder is 1:(0.92~0.99): (0.01~0.08);
Preferred, Me
2o, Ta
2o
5and Dy
2o
3the mol ratio of powder is 1:0.96:0.04;
Me
2o is Lithium Oxide 98min, sodium oxide, potassium oxide, a kind of in rubidium oxide and Cs2O.
Step S13, the powder taking is mixed to be dissolved in acidic solution, carry out crystallization treatment and obtain crystallisate in step S11, crystallisate is dissolved in solvent, then add ammoniacal liquor to regulate pH value to be 1~6, to obtain mixing solutions.
In this step, preferred, described fluorine-containing acidic solution comprises nitric acid, sulfuric acid or hydrochloric acid;
In this step, preferred, described solvent is the mixing solutions of distilled water or distilled water and dehydrated alcohol.
Step S15, described mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 150 ℃~500 ℃, be incubated 2 hours~10 hours, be precipitated thing, after being adopted to washings washing, the throw out obtaining is dried, then by dried throw out 800 ℃~1000 ℃ calcinations 0.5 hour~5 hours, obtaining dysprosium alkali-doped tantalate up-conversion luminescent material chemical general formula is MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
In this step, preferred, mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 300 ℃, is incubated 3 hours.
In this step, preferred, described washings is distilled water and dehydrated alcohol.
In this step, preferred, x is 0.04.
Hydrothermal method mild condition, the synthesis temperature of above-mentioned dysprosium alkali-doped tantalate up-conversion luminescent material are low more easy to control, and granularity and the pattern of product are controlled, the powder complete crystallization of preparation, good dispersity, cost is lower, produces comparatively environmental protection in simultaneous reactions process without the three wastes; In the photoluminescence spectra of the dysprosium alkali-doped tantalate up-conversion luminescent material of preparation, the excitation wavelength of dysprosium alkali-doped tantalate up-conversion luminescent material is 796nm, and the glow peak of the 482nm obtaining, is Dy
3+ion
4f
9/2→
6f
15/2transition radiation luminous, can be used as blue light emitting material.
Refer to Fig. 1, the Organic Light Emitting Diode 100 of an embodiment, this Organic Light Emitting Diode 100 comprises substrate 1, negative electrode 2, organic luminous layer 3, transparent anode 4 and the transparent encapsulated layer 5 stacking gradually.In transparent encapsulated layer 5, be dispersed with dysprosium alkali-doped tantalate up-conversion luminescent material 6, the chemical formula of dysprosium alkali-doped tantalate up-conversion luminescent material is MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
In the transparent encapsulated layer 5 of Organic Light Emitting Diode 100, be dispersed with dysprosium alkali-doped tantalate up-conversion luminescent material 6, dysprosium alkali-doped tantalate up-conversion luminescent material excitation wavelength be 796nm, the glow peak of the 482nm obtaining, is Dy
3+ion
4f
9/2→
6f
15/2transition radiation luminous, by red-green glow, excite and can launch blue light, after blue light mixes with red-green glow, form the Organic Light Emitting Diode emit white light.
Be specific embodiment below.
Embodiment 1
Select Li
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.96mmol, and 0.04mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 950 ℃ of conditions, and obtaining chemical general formula is LiTa
0.96o
3: 0.04Dy
3+up-conversion phosphor.
The substrate 1 that the preparation of Organic Light Emitting Diode stacks gradually uses soda-lime glass, negative electrode 2 to use metal A g layer, organic luminous layer 3 to use Ir (piq) 2 (acac) Chinese name to close iridium (III), transparent anode 4 use tin indium oxide ITO two (1-phenyl-isoquinoline 99.9) (methyl ethyl diketones), and transparent encapsulated layer 5 tetrafluoroethylene.In transparent encapsulated layer 5, be dispersed with dysprosium alkali-doped tantalate up-conversion luminescent material 6, the chemical formula of dysprosium alkali-doped tantalate up-conversion luminescent material is LiTa
0.96o
3: 0.04Dy
3+.
Refer to Fig. 2, Figure 2 shows that the dysprosium alkali-doped tantalate up-conversion luminescent material chemical general formula that this enforcement obtains is LiTa
0.96o
3: 0.04Dy
3+photoluminescence spectra figure.Fig. 2 is that the excitation wavelength of the dysprosium alkali-doped tantalate up-conversion luminescent material that obtains of the present embodiment is 796nm, in 482nm wavelength zone by Dy
3+ion
4f
9/2→
6f
15/2transition radiation form glow peak, this dysprosium alkali-doped tantalate up-conversion luminescent material can be used as blue light emitting material.
Refer to Fig. 3, in Fig. 3, curve is for implementing the XRD curve of the dysprosium alkali-doped tantalate up-conversion luminescent material of 1 preparation, test comparison standard P DF card.Contrast PDF card, shown in diffraction peak be depicted as the crystal orientation of alkali tantalate, there is not the relevant peak of neodymium ytterbium element, illustrate that two kinds of elements are the lattices that entered alkali tantalate.
Fig. 4 is the spectrogram of the Organic Light Emitting Diode that forms doped with dysprosium alkali-doped tantalate up-conversion luminescent material in the transparent encapsulated layer of embodiment 1 preparation, and curve 2 is not for adding the contrast of fluorescent material.In figure, can find out, fluorescent material can inspire the blue light of shortwave by the red light of long wave, blendes together white light.
Embodiment 2
Select Li
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.99mmol, and 0.01mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 1.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 150 ℃ of insulation 2h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 2 hours under 800 ℃ of conditions, and obtaining chemical general formula is LiTa
0.99o
3: 0.01Dy
3+up-conversion phosphor.
Embodiment 3
Select Li
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, and 0.92mmol and 0.08mmol mix.After mixing, in vitriolization solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 1000 ℃ of conditions, and obtaining chemical general formula is LiTa
0.92o
3: 0.08Dy
3+up-conversion phosphor.
Embodiment 4
Select Na
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.96mmol, and 0.04mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 950 ℃ of conditions, and obtaining chemical general formula is NaTa
0.96o
3: 0.04Dy
3+up-conversion phosphor.
Embodiment 5
Select Na
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.99mmol, and 0.01mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 1.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 150 ℃ of insulation 2h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 2 hours under 800 ℃ of conditions, and obtaining chemical general formula is NaTa
0.99o
3: 0.01Dy
3+up-conversion phosphor.
Embodiment 6
Select Na
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, and 0.92mmol and 0.08mmol mix.After mixing, in vitriolization solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 1000 ℃ of conditions, and obtaining chemical general formula is NaTa
0.92o
3: 0.08Dy
3+up-conversion phosphor.
Embodiment 7
Select K
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.96mmol, and 0.04mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 950 ℃ of conditions, and obtaining chemical general formula is KTa
0.96o
3: 0.04Dy
3+up-conversion phosphor.
Embodiment 8
Select K
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.99mmol, and 0.01mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 1.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 150 ℃ of insulation 2h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 2 hours under 800 ℃ of conditions, and obtaining chemical general formula is KTa
0.99o
3: 0.01Dy
3+up-conversion phosphor.
Embodiment 9
Select K
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, and 0.92mmol and 0.08mmol mix.After mixing, in vitriolization solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 1000 ℃ of conditions, and obtaining chemical general formula is KTa
0.92o
3: 0.08Dy
3+up-conversion phosphor.
Embodiment 10
Select Rb
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.96mmol, and 0.04mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 950 ℃ of conditions, and obtaining chemical general formula is RbTa
0.96o
3: 0.04Dy
3+up-conversion phosphor.
Embodiment 11
Select Rb
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.99mmol, and 0.01mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 1.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 150 ℃ of insulation 2h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 2 hours under 800 ℃ of conditions, and obtaining chemical general formula is RbTa
0.99o
3: 0.01Dy
3+up-conversion phosphor.
Embodiment 12
Select Rb
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, and 0.92mmol and 0.08mmol mix.After mixing, in vitriolization solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 1000 ℃ of conditions, and obtaining chemical general formula is RbTa
0.92o
3: 0.08Dy
3+up-conversion phosphor.
Embodiment 13
Select Cs
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.96mmol, and 0.04mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 950 ℃ of conditions, and obtaining chemical general formula is CsTa
0.96o
3: 0.04Dy
3+up-conversion phosphor.
Embodiment 14
Select Cs
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, 0.99mmol, and 0.01mmol mixes.After mixing, be dissolved in and in salpeter solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 1.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 150 ℃ of insulation 2h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 2 hours under 800 ℃ of conditions, and obtaining chemical general formula is CsTa
0.99o
3: 0.01Dy
3+up-conversion phosphor.
Embodiment 15
Select Cs
2o, Ta
2o
5and Dy
2o
3powder is 1mmol by each component mole number, and 0.92mmol and 0.08mmol mix.After mixing, in vitriolization solution, carry out crystallization treatment and obtain crystallisate, then crystallisate is dissolved in distilled water and in solution and adds ammoniacal liquor, regulating pH value is 5.Then mixing solutions is transferred in the stainless steel cauldron of teflon lined, at 300 ℃ of insulation 3h, be precipitated thing.Again ethanol and distilled water repetitive scrubbing for the throw out that obtains, evaporate to dryness at 100 ℃, dried throw out is put into retort furnace calcination 3 hours under 1000 ℃ of conditions, and obtaining chemical general formula is CsTa
0.92o
3: 0.08Dy
3+up-conversion phosphor.
The above embodiment has only expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (10)
1. a dysprosium alkali-doped tantalate up-conversion luminescent material, is characterized in that: have following chemical general formula MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.
2. dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 1, is characterized in that, described x is 0.04.
3. a preparation method for dysprosium alkali-doped tantalate up-conversion luminescent material, is characterized in that, comprises the following steps:
According to MeTa
1-xo
3: xDy
3+the stoichiometric ratio of each element takes Me
2o, Ta
2o
5and Dy
2o
3powder, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element;
The powder taking is mixed and is dissolved in acidic solution, carry out crystallization treatment and obtain crystallisate;
Crystallisate is dissolved in solvent, then add ammoniacal liquor to regulate pH value to be 1~6, to obtain mixing solutions; And
Described mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 150 ℃~500 ℃, be incubated 2 hours~10 hours, be precipitated thing, after being adopted to washings washing, the throw out obtaining is dried, then by dried throw out 800 ℃~1000 ℃ calcinations 0.5 hour~5 hours, obtaining chemical general formula is MeTa
1-xo
3: xDy
3+dysprosium alkali-doped tantalate up-conversion luminescent material.
4. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described x is 0.04.
5. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described mixing solutions is transferred in the stainless steel cauldron of tetrafluoroethylene lining, at 300 ℃, is incubated 3 hours.
6. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described crystallisate is dissolved in solvent, and wherein said solvent is the mixing solutions of distilled water or distilled water and dehydrated alcohol.
7. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described acidic solution is nitric acid, sulfuric acid or hydrochloric acid.
8. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described pH value is 5.
9. the preparation method of dysprosium alkali-doped tantalate up-conversion luminescent material according to claim 3, is characterized in that, described washings is distilled water and dehydrated alcohol.
10. an Organic Light Emitting Diode, comprise the substrate, negative electrode, organic luminous layer, anode and the transparent encapsulated layer that stack gradually, it is characterized in that, in described transparent encapsulated layer, doped with dysprosium alkali-doped tantalate up-conversion luminescent material, the chemical general formula of described dysprosium alkali-doped tantalate up-conversion luminescent material is MeTa
1-xo
3: xDy
3+, wherein, x is that 0.01~0.08, Me is elemental lithium, sodium element, potassium element, a kind of in rubidium element and cesium element.