CN104177006A - 一种空心砖及其制造方法 - Google Patents
一种空心砖及其制造方法 Download PDFInfo
- Publication number
- CN104177006A CN104177006A CN201410390946.3A CN201410390946A CN104177006A CN 104177006 A CN104177006 A CN 104177006A CN 201410390946 A CN201410390946 A CN 201410390946A CN 104177006 A CN104177006 A CN 104177006A
- Authority
- CN
- China
- Prior art keywords
- hollow brick
- cement
- mica powder
- rice hulls
- yellow sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种空心砖,所述空心砖包括以下原料:页岩、水泥、黄沙、云母粉和稻谷壳,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80-90︰13-18︰20-25︰10-14︰5-10。合理的原理搭配及组分配比保证双联转的强度高、重量轻。本发明还公开了一种空心砖的制造方法,无需焙烧,简化工序,节约能源。
Description
技术领域
本发明涉及一种空心砖及其制造方法。
背景技术
以前建筑使用的材料主要为红砖,是一种用粘土烧制的实心砖。这种砖需要使用的粘土非常多,占用了大量的土地资源,对当今的社会来说,这是一种资源的浪费。近些年,人们开始利用粉煤灰和粘合剂制造砖,同时,开发出了空心砖。这种砖砖体较轻,而且,不会造成土地资源的大量使用,可以充分利用废弃的材料,节能环保,但是砖体的强度和重量难以达到一个平衡的状态。
发明内容
本发明所要解决的问题是提供一种空心砖,强度高、重量轻。
为了解决上述技术问题,本发明采用如下技术方案:一种空心砖,所述空心砖包括以下原料:页岩、水泥、黄沙、云母粉和稻谷壳,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80-90︰13-18︰20-25︰10-14︰5-10。
改进的,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80︰18︰25︰10︰5。
改进的,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:90︰13︰20︰14︰10。
改进的,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:85︰15︰23︰12︰7。
本发明还提供了一种空心砖的制造方法,包括以下步骤:
步骤一:将页岩、水泥、黄沙、云母粉和稻谷壳经机械粉碎,按80-90︰13-18︰20-25︰10-14︰5-10混合并加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料24h,陈化后再搅拌,搅拌后混合物料中的含水率为8-13%;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:置于通风处养护。
有益效果:
采用上述技术方案后,该发明一种空心砖,采用了页岩、水泥、黄沙和云母粉及合理的组分配比,强度高,采用了稻谷壳减轻了砖体的重量。该发明一种空心砖的制造方法,无需焙烧,简化工序,节约能源。
具体实施方式
实施例一:
一种空心砖,所述空心砖包括以下原料:页岩、水泥、黄沙、云母粉和稻谷壳,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80︰18︰25︰10︰5。
一种空心砖的制造方法,包括以下步骤:
步骤一:将页岩、水泥、黄沙、云母粉和稻谷壳经机械粉碎,按80︰18︰25︰10︰5的质量比混合并加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料24h,陈化后再搅拌,搅拌后混合物料中的含水率为8-13%;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:置于通风处养护。
实施例二:
本实施例与实施例一的区别在于,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:90︰13︰20︰14︰10。
实施例三:
本实施例与实施例一的区别在于,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:85︰15︰23︰12︰7。
除上述优选实施例外,本发明还有其他的实施方式,本领域技术人员可以根据本发明作出各种改变和变形,只要不脱离本发明的精神,均应属于本发明所附权利要求所定义的范围。
Claims (5)
1.一种空心砖,其特征在于:所述空心砖包括以下原料:页岩、水泥、黄沙、云母粉和稻谷壳,所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80-90︰13-18︰20-25︰10-14︰5-10。
2.根据权利要求1所述的一种空心砖,其特征在于:所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:80︰18︰25︰10︰5。
3.根据权利要求1所述的一种空心砖,其特征在于:所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:90︰13︰20︰14︰10。
4.根据权利要求1所述的一种空心砖,其特征在于:所述页岩、水泥、黄沙、云母粉和稻谷壳的质量比为:85︰15︰23︰12︰7。
5.一种空心砖的制造方法,用于制造权利要求1所述的一种空心砖的制造方法,其特征在于:包括以下步骤:
步骤一:将页岩、水泥、黄沙、云母粉和稻谷壳经机械粉碎,按80-90︰13-18︰20-25︰10-14︰5-10的质量比混合并加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料24h,陈化后再搅拌,搅拌后混合物料中的含水率为8-13%;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:置于通风处养护。