CN103408933A - 一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法 - Google Patents
一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法 Download PDFInfo
- Publication number
- CN103408933A CN103408933A CN2013102545677A CN201310254567A CN103408933A CN 103408933 A CN103408933 A CN 103408933A CN 2013102545677 A CN2013102545677 A CN 2013102545677A CN 201310254567 A CN201310254567 A CN 201310254567A CN 103408933 A CN103408933 A CN 103408933A
- Authority
- CN
- China
- Prior art keywords
- psa
- additive
- silver
- reaction
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法,将含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液分散在水中形成胶体,再加入银前驱体,于20℃~30℃下进行紫外辐照,得到棕黑色固体PSA/Ag材料;以所述PSA/Ag材料为载体,以铁盐为引发剂,加入添加剂以及吡咯单体,在0~50℃下反应6~48h,反应终止后分离产物,将分离产物干燥后置于四氢呋喃溶液中浸泡12~48h,得到中空结构的高电活性Ag/PPy纳米材料。本发明所得中空材料电化学活性高,且工艺过程操作简便、成本低廉、无污染,因而在催化、光电、电磁、生物领域具有极大的应用前景。
Description
技术领域
本发明属于中空结构纳米复合材料领域,具体涉及一种高电活性纳米复合材料(Ag/PPy)的制备方法。
背景技术
中空结构纳米复合材料是一种具有特殊结构和功能的新型材料,在生物化学、催化、材料科学等领域具有特殊的应用前景。纳米金属银(Ag)作为纳米材料的一种,将其填充在导电高分子聚吡咯(PPy)中不仅可以延长纳米Ag在空气中的稳定性,保持纳米Ag的导电性能,还可以改善导电聚吡咯(PPy)的强度和加工性能。这种以导电高聚物包覆金属纳米粒子的纳米复合材料,一直是材料科学的研究热点。
Ag/PPy作为一种实体微球型材料,在纳米微电子电路、纳米器件等领域已经取得了较好的成果。但实体粒子Ag/PPy的密度较大,表面积较小,可控性较差。所以制备密度小、比表面积大、可控性好的中空结构纳米复合材料Ag/PPy非常重要。
目前,中空结构粒子一般是由相应的核壳结构粒子经过去核处理得到。聚(苯乙烯-丙烯酸)(PSA)微球作为生物医药领域里应用最多的高分子材料,是制备核壳结构纳米粒子常采用的模板。可以以PSA为模板,制备PSA/Ag/PPy核壳粒子,然后通过化学方法去除其内核粒子PSA得到中空结构的Ag/PPy。其中制备PSA/Ag核壳结构粒子的方法有很多,常用的有机械化学法、化学气相沉积法、溶胶-凝胶法,共沉积法,乳液聚合法,化学镀法等,但是这些方法反应条件要求较苛刻,中间步骤较多,制备过程繁复,且需要的试剂较多,因而制备成本也较高。
经过对现有技术的检索发现,中国专利CN102335750A(公开号)公开了两种制备PSA/Ag复合粒子的方法。一种是将Ag前驱体溶液控制在一定沸腾温度下,直接加入PSA粒子分散液和还原剂而得到,另一种是向PSA粒子分散液中加入Ag纳米粒子溶胶而制的。但是这两种方法都存在不足,第一种方法虽无需对PSA粒子进行预先表面修饰,但其制备出的Ag粒子的表面负载率相对较低;第二种方法采用化学还原法制备Ag纳米粒子溶胶时需选择不同的反应体系和反应条件,工艺比较繁琐,而选择市售的Ag纳米粒子制备纳米Ag溶胶虽方法简单,但是其价格也比较昂贵。
又经检索发现,中国专利CN102364616A(公开号)公开了一种在复合微球Fe3O4PS分散液中加入分散剂、还原剂和银氨溶液直接加热使Ag析出在PS微球表面的方法。该方法虽操作简单,但是该方法需要对Fe3O4PS粒子预先进行表面修饰,且生成的Ag容易团聚。
因此,开发一种工艺简单、成本低廉的高电活性的中空结构纳米复合材料(Ag/PPy)的制备方法,对推广中空粒子在催化、光电、电磁、生物等领域应用具有重要意义。
发明内容
本发明的目的是克服现有化学反应条件苛刻的制备技术,操作繁琐、设备昂贵、成本高等弊端,提供一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法。本发明以聚(苯乙烯-丙烯酸)为模板,采用紫外辐照法直接在聚(苯乙烯-丙烯酸)表面生成高电导率金属纳米Ag,该方法工艺简单,不需要进一步对聚(苯乙烯-丙烯酸)粒子表面进行特定的改性与修饰,且无需过多的药品,即可得到相应的核壳结构粒子。然后通过化学氧化法使核壳粒子外包覆一层导电高聚物,并通过去除其内核粒子得到密度小、比表面积大的中空结构的Ag/PPy。整个过程操作简便、成本低廉、无污染。
本发明的目的可以通过以下措施达到:
一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法,其包括如下步骤:
(1)将含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液分散在水中形成胶体,再加入银前驱体,于20℃~30℃下进行紫外辐照,得到棕黑色固体PSA/Ag材料;
(2)以所述PSA/Ag材料为载体,以铁盐为引发剂,加入添加剂以及吡咯单体,在0~50℃下反应6~48h,反应终止后分离产物,将分离产物干燥后置于四氢呋喃溶液中浸泡12~48h,得到中空结构的高电活性Ag/PPy纳米材料。
本发明中的添加剂选自丙烯酸、甲基丙烯酸、十二烷基硫酸钠(SDS)、聚乙烯吡咯烷酮(PVP)、对甲苯磺酸(p-TSA)、氨水中的一种或几种。进一步的,步骤(1)中的添加剂选自丙烯酸、甲基丙烯酸、十二烷基硫酸钠中的一种或几种,该添加剂的含量为聚(苯乙烯-丙烯酸)质量的0.01~0.1%,优选0.02~0.05%;步骤(2)中的添加剂选自十二烷基硫酸钠、聚乙烯吡咯烷酮、对甲苯磺酸中的一种或几种,该添加剂的质量为吡咯单体质量的20~60倍,优选45~55倍。
在步骤(1)中,所述银前驱体选自硝酸银、硫酸银或醋酸银。
在步骤(1)中,紫外辐照的时间优选5~10h。本发明对紫外辐照源无特定要求,一般采用274nm或330nm的紫外灯,实验时采用30W或50W的紫外灯。
在步骤(1)中,所述银前驱体加入胶体中后银前驱体的含量不大于0.0002mol/L;得到的PSA/Ag材料中Ag的质量含量为0.5~5%,优选0.8~2%。本发明提供的利用紫外辐照法氧化还原制备壳核结构纳米Ag/PPy材料在常温条件下,高电导率金属含量≤0.0002mol/L时,对金属的附着率可达到90~95%。
在步骤(2)中,铁盐选自硝酸铁、硫酸铁、氯化铁、水合硝酸铁、水合硫酸铁或水合氯化铁中的一种或几种;铁盐的用量为吡咯单体质量的2~8倍,优选3~6倍。
在步骤(2)中,PSA/Ag载体与吡咯单体的体积比为200~260:1,优选230~250:1。
在步骤(2)中,PSA/Ag材料与吡咯单体的反应优选在0~20℃下进行,反应时间优选为15~30h,反应后加入适当的乙醇以终止反应;反应终止后的分离产物优选在30~80℃下干燥6~48h。
本发明中的含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液可以直接采用向现有的纳米级聚(苯乙烯-丙烯酸)乳液中加入添加剂进行制得。其中现有的纳米级聚(苯乙烯-丙烯酸)乳液采用现有方法制备或直接采用商品化的纳米级乳液。本发明公开了一种含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液的制备方法,其包括如下步骤:
(a)将添加剂、苯乙烯和丙烯酸加入去离子水中,在引发剂作用下于60℃~90℃下反应,制备PSA种子乳液;其中苯乙烯与丙烯酸的体积比为10~13:1,优选11~12:1;反应在氮气保护下进行。
(b)取PSA种子乳液置于去离子水中,搅拌后加入引发剂并缓慢加入苯乙烯,最后加入丙烯酸并于60℃~80℃下进行搅拌反应,即得。其中苯乙烯与丙烯酸的体积比为10~13:1,优选11~12:1;反应在氮气保护下进行。
本发明的有益效果:
本发明利用紫外辐照法氧化还原制备壳核结构纳米聚合物金属材料。其原理是紫外辐照产生的水合电子,可以将微球表面负载的银离子还原为纳米晶核;再以附着在PSA表面的纳米Ag为银核,逐渐加入一定量的银离子,使Ag纳米晶核在胶球表面继续生长,得到Ag纳米,并逐步形成较为连续的壳层。最后在其表面通过化学还原法覆上一层高电导率聚合物。该材料具有对高电导率金属附着效果好、成本低、不易团聚等特点,并且相对化学镀以及其他金属还原方法具有绿色无毒害,操作工艺简单等优势。本发明所得中空材料电化学活性高,且工艺过程操作简便、成本低廉、无污染,因而在催化、光电、电磁、生物领域具有极大的应用前景。
附图说明
图1为具体实施例所制备的PSA(a)、PSA/Ag(b)、PSA/Ag/PPy(c)和Ag/PPy(d)的红外光谱。
在图1a中,1446、1496、1604cm-1处为单取代苯的环振动吸收峰,2920cm-1和3025cm-1对应苯环上不饱和C-H的伸缩振动峰;指纹区696和753cm-1处两个较强的吸收峰为苯环上C-H键面外弯曲振动;在1025cm-1还出现了单取代苯环上H原子的面内振动吸收峰;2848cm-1为亚甲基的吸收峰,这些特征峰说明苯乙烯发生聚合反应生成聚苯乙烯。此外,1718cm-1处对应着PAA中羧基中的C=O的伸缩振动峰,3445cm-1处-OH的伸缩振动峰进一步说明有羧基的存在。如图1b所示,由于纳米银与壳层PAA中-COOH中之间静电吸附作用,PSA/Ag复合微球在对应的1718cm-1处的特征吸收峰也相应减弱。红外分析表明,实验成功制备了PSA/Ag复合微球,且表明了纳米Ag是通过化学作用复合在微球表面,而非简单的混合。图1c所示为PSA/Ag/PPy的谱图,谱线上3432.20cm-1处较宽的谱带对应的是-OH、纳米Ag和N-H伸缩振动的吸收峰,从与图1b的对比上来看PSA/Ag/PPy在此处的峰谱峰的强度减弱了,并出现了红移,这可能是由于PPy掺杂的影响,1500和1447.38cm-1处是吡咯环的C-C和C-N伸缩振动吸收峰,说明吡咯环并未改变,1285.77cm-1处的吸收峰对应的是=C-H和N-H的平面内变形振动峰,1188.67cm-1对应的是C-N的伸缩振动吸收,1030.5cm-1为C-H变形振动吸收和N-H伸缩振动。红外分析表明,实验成功制备了PSA/Ag/PPy三组分核壳粒子。图1d所示为Ag/PPy的谱图,图中可以看出位于1950-1700cm-1的苯环的单取代特征吸收峰消失了,由此可以证明PSA微球被THF完全溶去,形成中空结构的Ag/PPy粒子。
图2为具体实施例所制备的纳米PSA/Ag、PSA/Ag/PPy、Ag/PPy的TEM图谱。
图2中,(a)加添加剂且高电导率金属含量≤0.0002mol/L所制备的PSA/Ag;(b)实施例3中未加添加剂但高电导率金属含量≤0.0002mol/L所制备的PSA/Ag;(c)实施例3中加添加剂但高电导率金属含量>0.0002mol/L所制备的PSA/Ag;(d)PSA/Ag/PPy;(e)中空Ag/PPy。如图2a所示,加添加剂且高电导率金属含量≤0.0002mol/L的情况所制得的PSA/Ag样品,可以看到微球表面均匀包覆着纳米Ag粒子,且Ag粒子相互之间没有连结,复合微球呈单分散。图2b所示为未加添加剂但高电导率金属含量≤0.0002mol/L所得的PSA/Ag样品,可以明显地观察到虽然有一定量的Ag附着在PSA微球表面上,但更多的Ag在微球表面发生了团聚现象。由此表明,一定量的添加剂能够使得Ag更好地分散在微球表面并得到单分散的Ag颗粒,还能够在一定程度上打破生成颗粒的团聚结构。图2c加添加剂但高电导率金属含量>0.0002mol/L所得的PSA/Ag样品,可以看到基底无残余Ag粒子,纳米Ag均包覆在微球表面,但由于高电导率金属含量过大使得产物出现了一定量的团聚,包覆的不够均匀,效果不如图2a。图2d是以PSA/Ag为模板所制备的PSA/Ag/PPy TEM表征图,可以看到PSA/Ag的表面均匀地附着了PPy。图2e是PSA/Ag/PPy通过四氢呋喃浸泡去掉内核后的产物Ag/PPy的TEM表征图,从图中可以看到分散均匀,粒径均一的中空微球,由此可说明Ag/PPy纳米复合材料的生成。
图3中,图谱中有Ag元素的吸收峰,而EDS能谱中该元素的峰值与该元素的浓度成正比,如表1所示,为该物质的元素质量比和摩尔比,这表明该物质中的除了碳元素外,银元素含量较大,进一步说明了纳米Ag包覆在了PSA表面,形成PSA/Ag复合微球。
表1PSA/Ag的元素分析表
元素 | C | Ag |
质量比(weight%) | 98.99 | 1.01 |
摩尔比(Atom%) | 99.89 | 0.11 |
图4为具体实施例4所制备的纳米PSA/Ag/PPy微球和中空Ag/PPy在磷酸缓冲溶液(pH=7.0)中的循环伏安图谱。
图4a为PSA/Ag/PPy微球在以N2除氧的0.2M磷酸缓冲溶液中(pH=7.0)的循环伏安图谱。在0.25V电位下可以观察到Ag的氧化峰,这一现象从另一角度说明了Ag被成功地负载在了样品中。另外,PSA和PPy在这个电位窗口下没有峰,图中所出现的另外的峰状图可能是由于电极基础电流过大造成的。图4b为中空Ag/PPy的循环伏安图谱,可以看到,只出现了一个明显的氧化峰,此峰为银纳米粒子的氧化峰,其氧化电位约为0.25V。
具体实施方式
采用红外光谱(FTIR,MB154S型)对产物的化学结构进行表征;核壳材料形貌及粒径大小表采用PHILIPS Tecnai12型透射电子显微镜(TEM)观察;采用JEOL日本电子公司的能谱分析(EDS,JCM-6000型)对产物的成分进行表征;电化学分析采用循环伏安法,使样品在水中分散2小时后,吸取10μl涂布在打磨后的石墨电极上放置自然晾干,以饱和甘汞电极为参比电极、铂电极为对电极,在以N2除氧的0.2M磷酸缓冲溶液中(pH=7.0)进行循环伏安扫描,扫描速率为0.1V/s。
下面对本发明的实施例作详细说明:本实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式和具体的操作过程,但本发明的保护范围不限于下述的实施例。
实施例1
将0.25g十二烷基硫酸钠(SDS),加入到80~120ml实验室自制去离子水中;加入已进行减压蒸馏除去阻聚剂后苯乙烯(St)23ml及丙烯酸(AA)2ml,搅拌10min后加入0.3g引发剂过硫酸钾(KPS),机械搅拌速率为400rpm,整个反应过程在N2气保护下进行,保温温度为75℃,时间为6h,制备PSA种子乳液。
实施例2
取上述种子乳液4ml于100ml去离子水中,充分搅拌后加入引发剂0.1g,取减压蒸馏除去阻聚剂后苯乙烯(St)23ml于恒压漏斗中以5~6s一滴的速度滴加苯乙烯,滴加完成后加入丙烯酸(AA)2ml,机械搅拌速率为400rpm,整个反应过程在N2气保护下进行,保温温度为70℃,时间为6h,制备单分散纳米聚(苯乙烯-丙烯酸)(PSA)微球。
实施例3
将上述实施例2的单分散聚(苯乙烯-丙烯酸)乳液冷至室温后高速离心,沉降洗涤,以除去残留的单体和离子,在去离子水中超声分散,使之成均匀乳液。取PSA乳液1ml于50ml水中,充分搅拌均匀;将高电导率金属硝酸银溶解于聚苯乙烯的胶体中(高电导率金属的含量≤0.0002mol/L);充分搅拌后置于紫外灯下,紫外灯管距离液面10cm。通过紫外辐照还原纳米银,辐照10小时,得到分散均匀,包覆完好的纳米聚苯乙烯/金属壳核粒子。取上述产物,经过滤,洗涤,低温干燥后,研磨成粉,即得产物。
本实施例制得的核壳结构单分散纳米聚苯乙烯材料,纳米银还原率高,并在聚苯乙烯微球上附着良好,还原率高,附着率大。
实施例4
取50ml实施例3的单分散纳米聚苯乙烯金属壳核粒子于锥形瓶中,加入0.21ml吡咯、0.1g PVP、10.1g p-TSA,磁力搅拌30min后加入引发剂六水合三氯化铁(FeCl3·6H2O)0.9g。常温反应24h后加一定量乙醇终止反应。对反应产物用乙醇和水多次洗涤后于真空干燥箱中60℃干燥48h,将干燥后的聚吡咯置于一定量四氢呋喃(THF)中浸泡24h,将用THF浸泡过的微球低温干燥后,研磨成粉,即得产物。
实施例5
将实施例2制备的PSA乳液和AgNO3溶液按照V(PSA)/n(AgNO3)=105的比例超声搅拌5min,取50ml混合溶液,保持温度为常温,滴加质量分数为32%的稀氨水至pH为8,置于紫外灯(λ=253.7nm)下辐照10h;即得PSA/Ag复合粒子模板。以上述制备的PSA/Ag模板50ml,与10.1g p-TSA、0.1g PVP和0.21ml吡咯混合超声搅拌5min,取100ml混合溶液,保持温度为常温,磁力搅拌30min后加入0.9g FeCl3·6H2O包覆均匀,继续磁力搅拌24h得到墨绿色的溶液;将所得产物抽滤,分别用丙酮和去离子水洗涤至滤液无色,即得PSA/Ag/PPy复合微球。将该产物置于四氢呋喃(THF)中浸泡24h,再分别用丙酮和去离子水洗涤产物至滤液为无色,即得Ag/PPy中空结构粒子。
Claims (10)
1.一种中空结构的高电活性纳米银/聚吡咯复合材料的制备方法,其特征在于包括如下步骤:
(1)将含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液分散在水中形成胶体,再加入银前驱体,于20℃~30℃下进行紫外辐照,得到棕黑色固体PSA/Ag材料;
(2)以所述PSA/Ag材料为载体,以铁盐为引发剂,加入添加剂以及吡咯单体,在0~50℃下反应6~48h,反应终止后分离产物,将分离产物干燥后置于四氢呋喃溶液中浸泡12~48h,得到中空结构的高电活性Ag/PPy纳米材料。
2.根据权利要求1所述的方法,其特征在于所述添加剂选自丙烯酸、甲基丙烯酸、十二烷基硫酸钠、聚乙烯吡咯烷酮、对甲苯磺酸、氨水中的一种或几种。
3.根据权利要求2所述的方法,其特征在于步骤(1)中的添加剂选自丙烯酸、甲基丙烯酸、十二烷基硫酸钠中的一种或几种,该添加剂的含量为聚(苯乙烯-丙烯酸)质量的0.01~0.1%;步骤(2)中的添加剂选自十二烷基硫酸钠、聚乙烯吡咯烷酮、对甲苯磺酸中的一种或几种,该添加剂的质量为吡咯单体质量的20~60倍。
4.根据权利要求1所述的方法,其特征在于在步骤(1)中,所述银前驱体选自硝酸银、硫酸银或醋酸银。
5.根据权利要求1所述的方法,其特征在于在步骤(1)中,紫外辐照源为30W或50W、274nm或330nm的紫外灯;紫外辐照时间为5~10h。
6.根据权利要求1所述的方法,其特征在于在步骤(1)中,所述银前驱体加入胶体中后银前驱体的含量不大于0.0002mol/L;得到的PSA/Ag材料中Ag的质量含量为0.5~5%。
7.根据权利要求1所述的方法,其特征在于所述铁盐选自硝酸铁、硫酸铁、氯化铁、水合硝酸铁、水合硫酸铁或水合氯化铁中的一种或几种;铁盐的用量为吡咯单体质量的2~8倍。
8.根据权利要求1所述的方法,其特征在于在步骤(2)中,PSA/Ag载体与吡咯单体的体积比为200~260:1,优选230~250:1;PSA/Ag材料与吡咯单体的反应在0~20℃下进行,反应时间为15~30h,反应后加入乙醇终止反应;反应终止后的分离产物需在30~80℃下干燥6~48h。
9.根据权利要求1所述的方法,其特征在于所述含有添加剂的纳米级聚(苯乙烯-丙烯酸)乳液由如下方法制备:
(a)将添加剂、苯乙烯和丙烯酸加入去离子水中,在引发剂作用下于60℃~90℃下反应,制备PSA种子乳液;
(b)取PSA种子乳液置于去离子水中,搅拌后加入引发剂并缓慢加入苯乙烯,最后加入丙烯酸并于60℃~80℃下进行搅拌反应,即得。
10.根据权利要求9所述的方法,其特征在于所述苯乙烯与丙烯酸的体积比为10~13:1,所述引发剂为过硫酸钾;步骤(a)和(b)的反应在氮气保护下进行。