CN103145442A - Method for preparing sintering-free ceramsite by using chemical sludge - Google Patents
Method for preparing sintering-free ceramsite by using chemical sludge Download PDFInfo
- Publication number
- CN103145442A CN103145442A CN2013101057074A CN201310105707A CN103145442A CN 103145442 A CN103145442 A CN 103145442A CN 2013101057074 A CN2013101057074 A CN 2013101057074A CN 201310105707 A CN201310105707 A CN 201310105707A CN 103145442 A CN103145442 A CN 103145442A
- Authority
- CN
- China
- Prior art keywords
- sludge
- ash
- dry blend
- roasting
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for preparing non-sintered ceramsite by using chemical sludge, belonging to the technical field of treatment and recycling of dangerous solid wastes in the chemical industry. Firstly, drying sludge to obtain dried sludge; then roasting and drying the sludge, and crushing the obtained sludge ash by using a crusher; mixing the sludge ash powder, the fly ash, the cement, the gypsum powder, the light material and the foaming agent in proportion, uniformly stirring, adding water, stirring, preparing spherical particles, and finally naturally curing to obtain the baking-free filler. The invention takes dangerous solid waste chemical sludge and industrial solid waste fly ash as main raw materials, and adopts a non-sintering process, and carries out natural maintenance in the later period, thereby having less equipment investment, simple process route and low energy consumption; the prepared ceramsite has high strength, large specific surface area, rough surface and more pores, the leaching toxicity of heavy metals is in accordance with GB5085.3-2007, and the ceramsite can be used for water treatment engineering.
Description
Technical field
The present invention relates to a kind of method of utilizing chemical engineering sludge to prepare non-sintered haydite, belong to that the chemical industry hazardous solid waste process to be disposed and the resource technology field.
Background technology
Chemical industry is polluted many and serious, and especially in the chemical wastewater treatment process, every annual meeting produces a large amount of excess sludges, and their complicated components contain poisonous and hazardous organism and heavy metal etc.For a long time, domestic ubiquity the tendency of the light mud of heavy water, and the safe disposal ability of mud is in lower level always.
The disposal options of existing chemical engineering sludge is mainly to burn, but the incineration disposal expense is high, and there are the problem of disposing capacity deficiency in many units, therefore, then mud is illegally shifted, topples over, and causes serious environmental pollution.The lime-ash that sludge incineration produces is also dangerous solid waste, generally needs first pre-treatment, then carries out security landfill.Therefore the processing costs of incineration residue is also very high, and a lot of enterprises are difficult to bear, then process as general solid waste, make sludge burning ash residue not obtain rational ultimate disposal, become important environment risk source, also reasonably do not fully utilized, caused the waste of resource.Sludge burning ash residue is carried out innoxious and resource utilization, turn waste into wealth, meet the requirement of recycling economy and Sustainable development, be extremely important.
Haydite take lytag as representative generally has the characteristics such as specific surface area is large, and porosity is large, and physical strength is high, and chemistry and biologically stable are good, has obtained using more and more widely in engineering of water treatment.The main chemical compositions of chemical engineering sludge lime-ash and flyash are very approaching, all belong to CaO-SiO
2-Al
2O
3-Fe
2O
3System, thereby have the utilization of resources.
The preparation method of present China haydite is take sintering process as main, but the agglomerating plant investment is large, and energy consumption is high, and production cost is improved, and has limited to a certain extent the development of haydite manufacturer.
Summary of the invention
The object of the invention is to provide in order to improve the deficiencies in the prior art that a kind of physical strength is high, specific surface area is large, chemistry and a kind of good method of utilizing chemical engineering sludge to prepare non-sintered haydite of biologically stable, this haydite utilizes chemical engineering sludge and industrial waste flyash, adopt non-sintered method, thereby investment reduces, energy efficient, reduce costs, for the recycling treatment of chemical engineering sludge has been opened up new approach.
Technical scheme of the present invention is: a kind of method of utilizing chemical engineering sludge to prepare non-sintered haydite, it is characterized in that, and concrete steps are as follows:
(1) dry chemical engineering sludge, obtain dewatered sludge;
(2) roasting dewatered sludge, gained mud lime-ash is pulverized with pulverizer;
(3) various raw materials are mixed by proportioning, the dry blend that stirs to get, the mass percent that wherein in dry blend, each component and each component account for the dry blend total amount is respectively: mud lime-ash 20%-50%, flyash 25%-40%, cement 10%-25%, gypsum 5%-15%, light material 1%-5%, whipping agent 0.2%-0.6%;
(4) add water also stirring, mixing in above-mentioned dry blend, its amount of water is the 30%-40% of dry blend weight;
(5) make spheroidal particle, its particle diameter is 5-10mm;
(6) natural curing 7-15 days.
Preferred described light material is pearlstone, rice husk or wood chip.Preferred selected whipping agent is aluminium powder or zinc powder.In preferred steps (1), the temperature of sludge-drying is 105-120 ℃, and be 8-24h time of drying.In preferred steps (2), the temperature of roasting dewatered sludge is 550 ℃-700 ℃, and roasting time is 20-40min.
In the present invention, the mud lime-ash is similar to the main chemical compositions of flyash, possesses potential pozzolanic activity.Cement provides an effective alkaline environment as exciting agent, with SiO
2And Al
2O
3Effect generates the compound with hydraulic gelling property, simultaneously the heavy metal in the mud lime-ash is had solidification.Adding of gypsum can be accelerated active SiO
2, A1
2O
3Reaction, simultaneously gypsum again can with A1
2O
3Reaction, the calcium sulphoaluminate gum material of the generation hydraulicity.Light material can reduce the density of haydite, makes it lightization, and has certain bioaffinity.Whipping agent can be given birth to the reaction releasing hydrogen gas with steeping in water for reconstitution in alkaline environment, make filler produce pore, forms light porous structure.
Beneficial effect:
Compare with traditional sludge treatment and haydite preparation method, have following advantage:
1, in the present invention, the mass percent of mud lime-ash reaches 20%~50%, and utilization ratio is high, has greatly solved the problem of outlet of chemical engineering sludge.
2, the flyash in the present invention is also industrial solid castoff, further embodies efficient recycling rate, and obviously good environmental benefit and economic benefit arranged, and has dissemination.
3, the present invention in the mud ash comprehensive utilization, has realized the curing to heavy metal, therefore has innoxious and double effects resource utilization.
4, the present invention adopts non-sintered technique, and the later stage is carried out natural curing, and facility investment is few, operational path is simple, and energy consumption is low.
5, the haydite intensity of the present invention's preparation is high, and specific surface area is large, surface irregularity, and hole is many; All more than 60%, Leaching Heavy Metals meets " Hazardous wastes judging standard leaching characteristic identification " and (GB5085.3-2007), can be used for engineering of water treatment to the fixed rate of each heavy metal.
Description of drawings
Fig. 1 is the SEM Electronic Speculum figure on the prepared pottery material surface of embodiment 1;
Fig. 2 is the SEN Electronic Speculum figure of the prepared haydite section of embodiment 1;
Fig. 3 is process flow diagram of the present invention.
Embodiment
Process flow diagram of the present invention is as shown in Figure 3:
Embodiment 1:
Get water ratio and be certain chemical plant excess sludge of 84%, 110 ℃ of dry 12h are placed in retort furnace in 700 ℃ of roasting 20min with dewatered sludge, cooling pulverize with pulverizer afterwards.Get respectively mud lime-ash 35g, flyash 20g, 32.5R composite Portland cement 10g, gypsum 5g, wood chip 1g, aluminium powder 0.4g, fully stirring and evenly mixing gets dry blend, adds water and accounts for dry blend quality 36%, stirring and evenly mixing, then make spherical haydite again, and its diameter is at 5-10mm.Haydite at normal temperature, protected under damp condition maintenance 10 days.Test, its tap density is 723kg/m
3, the 1h water-intake rate is that 28.5%, BET specific surface area is 30.801m
2/ g, ultimate compression strength is 3.2MPa.Prepared pottery material surface and the SEM Electronic Speculum figure of section can find out on scheming as depicted in figs. 1 and 2: non-sintered haydite is surperficial and inside is coarse, numerous micro channels are arranged, and this structure is highly beneficial to adhering to, growing of microorganism.
Embodiment 2:
Get water ratio and be certain chemical plant excess sludge of 89%, 105 ℃ of dry 24h are placed in retort furnace in 600 ℃ of roasting 30min with dewatered sludge, cooling pulverize with pulverizer afterwards.Get respectively mud lime-ash 35g, flyash 40g, 32.5R composite Portland cement 15g, gypsum 10g, pearlstone 3g, zinc powder 0.4g, fully stirring and evenly mixing gets dry blend, adds water and accounts for 32% of dry blend quality, stirring and evenly mixing, then make spherical haydite again, and its diameter is in the 5-10mm left and right.Haydite at normal temperature, protected under damp condition maintenance 7 days.Test, its tap density is that tap density is 785kg/m
3, the 1h water-intake rate is that 25.7%, BET specific surface area is 21.175m
2/ g, resistance to compression Compressive Strength are 3.5Mpa.
Embodiment 3:
Get water ratio and be certain chemical plant excess sludge of 78%, 120 ℃ of dry 8h are placed in retort furnace in 550 ℃ of roasting 40min with dewatered sludge, cooling pulverize with pulverizer afterwards.Get respectively mud lime-ash 20g, flyash 35g, 32.5R composite Portland cement 25g, gypsum 15g, rice husk 5g, aluminium powder 0.21g, fully stirring and evenly mixing gets dry blend, adds water and accounts for 38% of dry blend quality, stirring and evenly mixing, then make spherical haydite again, and its diameter is in the 5-10mm left and right.Haydite at normal temperature, protected under damp condition maintenance 15 days.Test, its tap density is 826kg/m
3, the 1h water-intake rate is that 20.3%, BET specific surface area is 9.117m
2/ g, ultimate compression strength is 4.1Mpa.
The comparison of the non-sintered haydite Leaching Heavy Metals of table 1 and " Hazardous wastes judging standard leaching characteristic identification "
Claims (5)
1. a method of utilizing chemical engineering sludge to prepare non-sintered haydite, is characterized in that, concrete steps are as follows:
(1) dry chemical engineering sludge, obtain dewatered sludge;
(2) roasting dewatered sludge, gained mud lime-ash is pulverized with pulverizer;
(3) various raw materials are mixed by proportioning, the dry blend that stirs to get, the mass percent that wherein in dry blend, each component and each component account for the dry blend total amount is respectively: mud lime-ash 20%-50%, flyash 25%-40%, cement 10%-25%, gypsum 5%-15%, light material 1%-5%, whipping agent 0.2%-0.6%;
(4) add water also stirring, mixing in above-mentioned dry blend, its amount of water is the 30%-40% of dry blend weight;
(5) make spheroidal particle, its particle diameter is 5-10mm;
(6) natural curing 7-15 days.
2. method according to claim 1, is characterized in that described light material is pearlstone, rice husk or wood chip.
3. method according to claim 1, is characterized in that selected whipping agent is aluminium powder or zinc powder.
4. method according to claim 1, is characterized in that the temperature of sludge-drying in step (1) is 105-120 ℃, and be 8-24h time of drying.
5. method according to claim 1, is characterized in that the temperature of roasting dewatered sludge in step (2) is 550 ℃-700 ℃, and roasting time is 20-40min.