CN103045039A - 一种防静电材料及其制备方法 - Google Patents
一种防静电材料及其制备方法 Download PDFInfo
- Publication number
- CN103045039A CN103045039A CN2012105879656A CN201210587965A CN103045039A CN 103045039 A CN103045039 A CN 103045039A CN 2012105879656 A CN2012105879656 A CN 2012105879656A CN 201210587965 A CN201210587965 A CN 201210587965A CN 103045039 A CN103045039 A CN 103045039A
- Authority
- CN
- China
- Prior art keywords
- solvent
- antistatic material
- resinous varnish
- static
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种防静电材料,该防静电材料包括树脂清漆、溶剂、醇溶剂和聚苯乙烯磺酸钠,所述树脂清漆固含物的含量为25%,溶剂的含量为50%~67%,醇溶剂的含量为7.5%~23%,聚苯乙烯磺酸钠固含物的含量为0.5%~2%。一种前述防静电材料的制备方法,依次加入聚苯乙烯磺酸钠、醇溶剂、溶剂和树脂清漆,并搅拌均匀,得到所述防静电材料。本发明防静电材料抗静电效果持久,为普通小分子抗静电剂使用时间的五倍以上;本发明防静电材料表面电阻值稳定,最低可达105欧姆;本发明防静电材料抗静电效果不受环境温度、湿度的影响;本发明防静电材料在电子包装行业可以重复利用,有效降低了企业的生产成本。
Description
技术领域
本发明涉及化学材料领域,特别涉及一种高分子聚合物的防静电材料及其制备方法。
背景技术
抗静电的方法有两种:一种是减轻或抑制其起电;另一种是将产生的静电迅速泄露以减少静电的大量积累。抗静电剂就是指能抑制静电产生和促进电荷泄露以防止或消除高分子材料表面静电积累的一类化学物质。抗静电剂品种很多,按其亲水基能否电离和电离后所带电荷性质的不同,可分为阴离子型、阳离子型、两性型和非离子型抗静电剂。
阴离子型抗静电剂多用作化纤油剂和油品的抗静电剂,在塑料工业中除某些烷基磷酸(或硫酸)酯用于聚氯乙烯(Pvc)和聚烯烃作内混型抗静电剂使用外,大多用作外涂型抗静电剂。但此类抗静电剂对透明制品有不利影响。
阳离子型抗静电剂极性高,抗静电效果较好,但热稳定性差,且对热敏性树脂的热稳定性有不良影响,也存在不同程度的毒性或刺激性。
两性型抗静电剂最大特点是分子内同时含有阳离子和阴离子基团,在一定条件下可同时显示阳离子型和阴离子型抗静电剂作用,在应用中与其他类型抗静电剂配合使用,但热稳定性较差,不可靠。
非离子型抗静电剂虽然热稳定性优异,一般对高分子材料不产生有害影响,多数产品无毒或低毒,但其本身不能离解为离子,无法通过自身导电来泄漏电荷,抗静电效果不及离子型抗静电剂。
以上四种抗静电剂均为小分子物质,化学性能不稳定,受环境温度、湿度的影响较大,而且在耐水洗方面效果也不好。因此,如何提高抗静电剂的化学稳定性,减少环境对其影响,增强其耐水洗性成为防静电材料领域亟待解决的问题。
发明内容
为了解决现有防静电剂化学性能不稳定,受环境影响大,耐水洗性能差的问题,本发明提出以下技术方案:
一种防静电材料,该防静电材料包括树脂清漆、溶剂、醇溶剂和聚苯乙烯磺酸钠,所述溶剂为酮类、脂类或者苯类中的至少一种,所述树脂清漆固含物的含量为25%,溶剂的含量为50%~67%,醇溶剂的含量为7.5%~23%,聚苯乙烯磺酸钠固含物的含量为0.5%~2%。
作为本发明的一种优选方案,所述树脂清漆为丙烯酸酯类、聚酯类或者聚氨酯类。
作为本发明的另一种优选方案,所述树脂清漆为丙烯酸酯类时,溶剂为环己酮或者二甲苯中的至少一种。
作为本发明的又一种优选方案,所述树脂清漆为聚酯类或者聚氨酯类时,溶剂为环己酮、二甲苯或者醋酸丁酯中的至少一种。
作为本发明的再一种优选方案,所述醇溶剂为甲醇、乙醇或者异丙醇中的至少一种。
一种前述防静电材料的制备方法,所述制备方法包括以下步骤:
A、将聚苯乙烯磺酸钠和醇溶剂加入到容器中,并进行搅拌,使其混合均匀;
B、将溶剂加入所述步骤A得到的混合液中,并进行搅拌,使其混合均匀;
C、将树脂清漆加入所述步骤B得到的混合溶液中,并进行搅拌,使其混合均匀,得到所述防静电材料。
本发明带来的有益效果是:
1、本发明防静电材料抗静电效果持久,为普通小分子抗静电剂使用时间的五倍以上;
2、本发明防静电材料表面电阻值稳定,最低可达10
5
欧姆,而含有小分子抗静电剂的抗静电材料,表面电阻值为10
9
~10
12
欧姆,甚至无效果;
3、本发明防静电材料抗静电效果不受环境温度、湿度的影响,而含有小分子抗静电剂的抗静电材料受环境温度、湿度的影响很大,特别是湿度的影响,在干燥的环境中,起不到任何抗静电的作用;
4、本发明防静电材料在电子包装行业可以重复利用,有效降低了企业的生产成本。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
一种防静电材料,该防静电材料包括树脂清漆、溶剂、醇溶剂和聚苯乙烯磺酸钠,溶剂为酮类、脂类或者苯类中的至少一种,树脂清漆固含物的含量为25%,溶剂的含量为50%~67%,醇溶剂的含量为7.5%~23%,聚苯乙烯磺酸钠固含物的含量为0.5%~2%。
其中,树脂清漆为丙烯酸酯类、聚酯类或者聚氨酯类。当树脂清漆为丙烯酸酯类时,溶剂为环己酮或者二甲苯中的至少一种。当树脂清漆为聚酯类或者聚氨酯类时,溶剂为环己酮、二甲苯或者醋酸丁酯中的至少一种。醇溶剂为甲醇、乙醇或者异丙醇中的至少一种。
按照不同的原料比例制备本发明防静电材料,制备方法1:
原料准备:取固含量为60%的丙烯酸脂清漆125g,环己酮150g,甲醇69g以及固含量为25%的聚苯乙烯磺酸钠24g。
首先,将聚苯乙烯磺酸钠和甲醇加入到容器中,并进行搅拌,直至其混合均匀为止;
其次,将环己酮加入上一步骤得到的混合液中,并进行搅拌,直至其混合均匀为止;
最后,将丙烯酸脂清漆加入上一步骤得到的混合溶液中,并进行搅拌,使其混合均匀,得到所述防静电材料。
该防静电材料中,树脂清漆、溶剂、醇溶剂以及聚苯乙烯磺酸钠的含量分别为25%、50%、23%和2%。将该防静电材料涂布在PET片材上,在100℃条件下干燥30min,表面电阻达10
5
~10
8
欧姆。
按照不同的原料比例制备本发明防静电材料,制备方法2:
原料准备:取固含量为60%的聚氨酯清漆125g,醋酸丁酯183g,乙醇39g以及固含量为25%的聚苯乙烯磺酸钠12g。
首先,将聚苯乙烯磺酸钠和甲醇加入到容器中,并进行搅拌,直至其混合均匀为止;
其次,将环己酮加入上一步骤得到的混合液中,并进行搅拌,直至其混合均匀为止;
最后,将丙烯酸清漆加入上一步骤得到的混合溶液中,并进行搅拌,使其混合均匀,得到所述防静电材料。
该防静电材料中,树脂清漆、溶剂、醇溶剂以及聚苯乙烯磺酸钠的含量分别为25%、61%、13%和1%。将该防静电材料涂布在PET片材上,在100℃条件下干燥30min,表面电阻达10
8
~10
10
欧姆。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (6)
1.一种防静电材料,其特征在于:该防静电材料包括树脂清漆、溶剂、醇溶剂和聚苯乙烯磺酸钠,所述溶剂为酮类、脂类或者苯类中的至少一种,为所述树脂清漆固含物的含量25%,溶剂的含量为50%~67%,醇溶剂的含量为7.5%~23%,聚苯乙烯磺酸钠固含物的含量为0.5%~2%。
2.根据权利要求1所述的一种防静电材料,其特征在于:所述树脂清漆为丙烯酸酯类、聚酯类或者聚氨酯类。
3.根据权利要求2所述的一种防静电材料,其特征在于:所述树脂清漆为丙烯酸酯类时,溶剂为环己酮或者二甲苯中的至少一种。
4.根据权利要求2所述的一种防静电材料,其特征在于:所述树脂清漆为聚酯类或者聚氨酯类时,溶剂为环己酮、二甲苯或者醋酸丁酯中的至少一种。
5.根据权利要求1所述的一种防静电材料,其特征在于:所述醇溶剂为甲醇、乙醇或者异丙醇中的至少一种。
6.一种权利要求1所述的防静电材料的制备方法,其特征在于:所述制备方法包括以下步骤:
A、将聚苯乙烯磺酸钠和醇溶剂加入到容器中,并进行搅拌,使其混合均匀;
B、将溶剂加入所述步骤A得到的混合液中,并进行搅拌,使其混合均匀;
C、将树脂清漆加入所述步骤B得到的混合溶液中,并进行搅拌,使其混合均匀,得到所述防静电材料。