CN102230119B - TiC系钢结硬质合金及其制备方法 - Google Patents
TiC系钢结硬质合金及其制备方法 Download PDFInfo
- Publication number
- CN102230119B CN102230119B CN 201110170310 CN201110170310A CN102230119B CN 102230119 B CN102230119 B CN 102230119B CN 201110170310 CN201110170310 CN 201110170310 CN 201110170310 A CN201110170310 A CN 201110170310A CN 102230119 B CN102230119 B CN 102230119B
- Authority
- CN
- China
- Prior art keywords
- tic
- powder
- percent
- iron
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
抗弯强度(Mpa) | 硬度(HRA) | 密度(g/cm3) | 金相组织 | |
实施例1 | 1550 | 87.5 | 5.95 | A04B02C00E00 |
实施例2 | 1200 | 91.5 | 5.52 | A04B04C00E00 |
实施例3 | 1690 | 87.8 | 5.93 | A02B00C00E00 |
实施例4 | 1500 | 89.5 | 5.72 | A02B00C00E00 |
实施例5 | 1250 | 91.0 | 5.51 | A04B00C00E00 |
TM52 | 1620 | 85.8 | 6.20 | A04B04C00E00 |
YT5 | 1560 | 90.5 | 12.98 | A04B02C00E00 |
Claims (3)