CN101478841B - Carbon/carbon heating body preparation method for polysilicon hydrogenation furnace - Google Patents

Carbon/carbon heating body preparation method for polysilicon hydrogenation furnace Download PDF

Info

Publication number
CN101478841B
CN101478841B CN2008102365461A CN200810236546A CN101478841B CN 101478841 B CN101478841 B CN 101478841B CN 2008102365461 A CN2008102365461 A CN 2008102365461A CN 200810236546 A CN200810236546 A CN 200810236546A CN 101478841 B CN101478841 B CN 101478841B
Authority
CN
China
Prior art keywords
carbon
charcoal
heating body
heating unit
hydrogenation furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008102365461A
Other languages
Chinese (zh)
Other versions
CN101478841A (en
Inventor
李永军
侯卫权
肖志超
苏君明
彭志刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chaoma Science & Technology Co Ltd Xian
Original Assignee
Chaoma Science & Technology Co Ltd Xian
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chaoma Science & Technology Co Ltd Xian filed Critical Chaoma Science & Technology Co Ltd Xian
Priority to CN2008102365461A priority Critical patent/CN101478841B/en
Publication of CN101478841A publication Critical patent/CN101478841A/en
Application granted granted Critical
Publication of CN101478841B publication Critical patent/CN101478841B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a method for preparing carbon/carbonate heating unit applied to a polysilicon hydrogenation furnace, wherein, a pinpricked plain wave carbon cloth quasi-three-needle structure prefabricated body is adopted; the prefabricated body is compacted through chemical vapor infiltration and the compaction processing is carried out repeatedly for several times; when the density is bigger than or equal to 1.30g/cm<3>, the compacting craft is over; mechanical processing is carried out after a high temperature treatment; then, CVD coating is carried out on the surface to obtain the carbon/carbonate heating unit. The method for preparing carbon/carbonate heating unit applied to a polysilicon hydrogenation furnace has the advantage that with the adoption of a craft method of chemical vapor infiltration, the carbon/carbonate heating unit is compactly obtained, thus can effectively improve purity and resistance of the heating unit in respect of the heating unit applied to the polysilicon hydrogenation furnace, improve anti-scouring capability and anticorrosion capacity of the heating unit, prolong service life of the heating unit and lower replacement rate of the heating unit.

Description

A kind of polysilicon hydrogenation furnace is with the preparation method of charcoal/carbon/carbon heating body
Technical field
The invention belongs to polysilicon hydrogenation furnace and use the heater technical field, be specifically related to the preparation method of a kind of polysilicon hydrogenation furnace with charcoal/carbon/carbon heating body.
Background technology
At present, the main method of producing polysilicon is the improvement Siemens Method, adopts the polysilicon of improvement Siemens Method production to account for more than 80% of global polysilicon total output.When the improvement Siemens Method was produced polysilicon product, hydrogenation furnace was that the circulatory system is the step that product reclaims, and was about to generate the accessory substance SiCl that the polysilicon product reaction produces 4With H 2Reaction generates SiHCl 3Raw material utilizes again.In the hydrogenation furnace, under 1250 ℃ of conditions, SiCl 4With H 2Mist get in the stove with the speed of 30m/s and react, furnace pressure reaches 0.6MPa.Therefore require heater purity high, do not pollute polysilicon product, have higher resistance value (0.06~0.25 Ω), high anti-the washing away of intensity.The hydrogenation furnace continuous operating time is more than 2000 hours, so will have a strong impact on the continuous operating time of hydrogenation furnace the useful life of heater.
Chinese patent ZL200610043185X; Name is called and discloses the employing needled carbon cloth in " monocrystalline silicon draw machines and polysilicon smelting furnace are with the preparation method of charcoal/charcoal heater " and combine with no latitude cloth and process full charcoal fiber three-dimensional structure heater precast body; Matrix adopting asphalt carbon and resin charcoal double element carbon matrix; And under the condition in 2000~2500 ℃ of logical chlorine and fluorine Lyons, carry out purification process; Its weak point is that (1) all is made up of long charcoal fiber owing to the heater precast body, electric conductivity asphalt carbon component is preferably arranged again in the carbon matrix, and temperature surpasses the purification process more than 2000 ℃; The resistance value of its charcoal/carbon/carbon heating body is merely 0.016~0.020 Ω, than the little one magnitude of required value; (2) do not adopt vacuum pressed dipping technique scheme when furfural acetone resin or resin impregnating, dipping efficient on the low side 30%.
Russia makes polysilicon hydrogenation furnace and adopts charcoal cloth lamination precast body with charcoal/carbon/carbon heating body; Through isothermal method chemical vapor infiltration technology densified; Its weak point is: (1) charcoal cloth lamination precast body is prone to the thickness direction lamination defect in process of production, and rate of finished products is low; (2) content of ashes is high, is generally 2000~4000ppm, is inappropriate for the applications that requires purity high.
Germany makes polysilicon hydrogenation furnace and adopts no latitude cloth lamination precast body with charcoal/carbon/carbon heating body, makes rectangular flat plate with the bituminizing pressurization, uses the graphite bolt that two rectangular flat plate are connected with the high purity graphite piece and processes.Its weak point: (1) graphite bolt strength is lower, adopts bolted to connect, and causes the coupling part contact resistance bigger, causes the heater local temperature inhomogeneous in the course of the work, thereby causes the inhomogeneous of the interior thermal field of hydrogenation furnace; (2) heater is that three parts are formed, and comparatively inconvenience is installed, and damages easily.
Summary of the invention
Technical problem to be solved by this invention is to above-mentioned deficiency of the prior art; The preparation method of the simple polysilicon hydrogenation furnace of a kind of technology with charcoal/carbon/carbon heating body is provided; Fine and close respond well to prepare; Have high resistance and high purity, thermal shock resistance and structural stability are good, and the polysilicon hydrogenation furnace of long service life is with charcoal/carbon/carbon heating body.
For solving the problems of the technologies described above, technical scheme of the present invention is: a kind of polysilicon hydrogenation furnace is characterized in that with the preparation method of charcoal/carbon/carbon heating body the preparation process is:
(1) adopt charcoal cloth and short carbon fiber net tire alternative stacked, constitute plane fibers, introduce vertical fibers at the thickness direction employing needling process of plane fibers, process three-dimensional structure heater precast body, the density of precast body is 0.25~0.65g/cm 3
(2) chemical gas-phase permeation compaction technology: adopt the graphite frock with the inside and outside typing of the three-dimensional structure heater precast body in the step (1); With propylene or natural gas be raw material high temperature 850-1200 ℃ of following cracking, three-dimensional structure heater precast body is carried out gas-phase permeation compaction handles;
(3) condition of high vacuum degree high temperature purification treatment technology: the density>=1.30g/cm of the three-dimensional structure heater precast body in the step (2) 3The time, in vaccum sensitive stove, said three-dimensional structure heater precast body being carried out the condition of high vacuum degree high temperature purification treatment, said high temperature is meant that temperature is 1500-2300 ℃, said condition of high vacuum degree is meant vacuum degree≤40Pa; Density<the 1.30g/cm of the three-dimensional structure heater in the step (2) 3The time, return to step (2);
(4) mechanical processing technique: to process drilling machine boring in the step (3) with milling machine through the charcoal/carbon/carbon heating body of condition of high vacuum degree high temperature purification treatment;
(5) chemical vapor deposited coatings being carried out on the charcoal after machining/carbon/carbon heating body surface in the step (4) handles; Promptly make high resistance and high-purity polycrystalline hydrogenation furnace with charcoal/carbon/carbon heating body; Said high resistance is meant that resistance value is 0.06~0.25 Ω, and said high-purity is meant ash content≤800ppm.
Charcoal cloth described in the above-mentioned steps (1) is 6-48K plain weave charcoal cloth, and wherein K represents tow thousand radicals.
The resistivity of the charcoal/carbon/carbon heating body in the above-mentioned steps (3) after the condition of high vacuum degree high temperature purification treatment is 25~60 μ Ω m.
The treatment temperature of surface chemistry vapour deposition coating is 900-1200 ℃ described in the above-mentioned steps (5).
The width of said charcoal/carbon/carbon heating body is 60~200mm, highly is 1000~4000mm.
The present invention compared with prior art has the following advantages:
(1) adopts acupuncture 6~48K charcoal cloth and short carbon fiber net tire alternative stacked to make three-dimensional structure heater precast body, suitably reduce long stapled content, improved the resistance value of charcoal/carbon/carbon heating body; And short carbon fiber net tire provides the silk source of acupuncture vertical fibers, has increased the content of vertical fibers, has improved the ability of the anti-layering of precast body densification technique process;
(2) densification technique of employing chemical vapor infiltration, fine and close respond well, the deposit carbon Stability Analysis of Structures has good dimensional stability.
(3) adopt 1500-2300 ℃ high vacuum high temperature purification treatment, under the prerequisite that does not reduce charcoal/carbon/carbon heating body resistance value, can improve product purity again, and can improve thermal shock resistance and structural stability greatly.
(4) the heater product after the machine work is carried out surface chemistry vapour deposition (CVD) coating and handle, can effectively improve the erosion resistibility of heater product and at SiCl 4, the corrosion resistance in the HCl atmosphere.
(5) global formation, it is convenient to install, and not fragile, the useful life of ability significant prolongation charcoal/carbon/carbon heating body.
Through accompanying drawing and embodiment, technical scheme of the present invention is done further detailed description below.
Description of drawings
Fig. 1 is a process chart of the present invention.
Fig. 2 is the polysilicon hydrogenation furnace of the present invention preparation front view with charcoal/carbon/carbon heating body.
Fig. 3 is the left view of Fig. 2.
Fig. 4 prepares polysilicon hydrogenation furnace with the structural representation of charcoal/carbon/carbon heating body with the graphite frock for the present invention.
Embodiment
Embodiment 1
(1) adopt 6K charcoal cloth and short carbon fiber net tire alternative stacked to constitute the in-plane fiber, adopt needling process to introduce vertical fibers at thickness direction, process three-dimensional structure heater precast body, its density is 0.65g/cm 3
(2) chemical vapor infiltration technology adopts the graphite frock with finalizing the design inside and outside the heater precast body, guarantees finished size; Under 850 ℃ of temperature, be that raw material carries out the gas-phase permeation compaction processing to precast body with the propylene;
(3) charcoal/carbon/carbon heating body extrudate density<1.30g/cm 3The time, repeating step (2) is as its density>=1.30g/cm 3The time, densification technique finishes;
(4) condition of high vacuum degree high temperature purification treatment: charcoal/carbon/carbon heating body goods are packed in the vaccum sensitive stove, and treatment temperature is 1500 ℃, vacuum degree≤5Pa;
(5) machining: to process drilling machine boring in the step (4) with milling machine through charcoal/carbon/carbon heating body after the purification process;
(6) chemical vapour deposition (CVD) (being CVD) coating being carried out on the heater surface and handle, under 900 ℃, is that raw material carries out the CVD carbon coating to the surface and promptly makes polysilicon hydrogenation furnace with charcoal/carbon/carbon heating body with the propylene.
Polysilicon hydrogenation furnace in the above-mentioned steps (6) uses the width of charcoal/carbon/carbon heating body to be 60mm, highly is 1000mm.
Embodiment 2
(1) adopt 12K charcoal cloth and short carbon fiber net tire alternative stacked to constitute the in-plane fiber, adopt needling process to introduce vertical fibers at thickness direction, process three-dimensional structure heater precast body, its density is 0.45g/cm 3
(2) chemical vapor infiltration technology adopts the graphite frock with finalizing the design inside and outside the heater precast body, guarantees finished size; Under 1040 ℃ of temperature, be that raw material carries out the gas-phase permeation compaction processing to precast body with the natural gas;
(3) charcoal/carbon/carbon heating body extrudate density<1.30g/cm 3The time, repeating step (2) is as its density>=1.30g/cm 3The time, densification technique finishes;
(4) condition of high vacuum degree high temperature purification treatment: charcoal/carbon/carbon heating body goods are packed in the vaccum sensitive stove, and temperature is 2000 ℃, vacuum degree≤20Pa;
(5) machining: to process drilling machine boring in the step (4) with milling machine through charcoal/carbon/carbon heating body after the purification process;
(6) chemical vapor deposited coatings being carried out on the heater surface and handle, under 980 ℃, is that raw material carries out the CVD carbon coating to the surface and promptly makes polysilicon hydrogenation furnace with charcoal/carbon/carbon heating body with the propylene.
Polysilicon hydrogenation furnace in the above-mentioned steps (6) uses the width of charcoal/carbon/carbon heating body to be 100mm, highly is 2000mm.
Embodiment 3
(1) adopt 48K charcoal cloth and short carbon fiber net tire alternative stacked to constitute the in-plane fiber, adopt needling process to introduce vertical fibers at thickness direction, process three-dimensional structure heater precast body, its density is 0.25g/cm 3
(2) chemical vapor infiltration technology adopts the graphite frock with finalizing the design inside and outside the heater precast body, guarantees finished size; Under 1200 ℃ of temperature, be that raw material carries out the gas-phase permeation compaction processing to precast body with the natural gas;
(3) charcoal/carbon/carbon heating body extrudate density<1.30g/cm 3The time, repeating step (2) is as its density>=1.30g/cm 3The time, densification technique finishes;
(4) condition of high vacuum degree high temperature purification treatment: charcoal/carbon/carbon heating body goods are packed in the vaccum sensitive stove, and temperature is 2300 ℃, vacuum degree≤40Pa;
(5) machining: to process drilling machine boring in the step (4) with milling machine through charcoal/carbon/carbon heating body after the purification process;
(6) chemical vapor deposited coatings being carried out on the heater surface and handle, under 1200 ℃, is that raw material carries out the CVD carbon coating to the surface and promptly makes polysilicon hydrogenation furnace with charcoal/carbon/carbon heating body with the natural gas.
Polysilicon hydrogenation furnace in the above-mentioned steps (6) uses the width of charcoal/carbon/carbon heating body to be 200mm, highly is 4000mm.
The above; It only is preferred embodiment of the present invention; Be not that the present invention is done any restriction, every technical spirit changes any simple modification, change and the equivalence that above embodiment did according to the present invention, all still belongs in the protection range of technical scheme of the present invention.

Claims (2)

1. a polysilicon hydrogenation furnace is characterized in that with the preparation method of charcoal/carbon/carbon heating body the preparation process is:
(1) adopt charcoal cloth and short carbon fiber net tire alternative stacked, constitute plane fibers, introduce vertical fibers at the thickness direction employing needling process of plane fibers, process three-dimensional structure heater precast body, the density of precast body is 0.25~0.65g/cm 3Said charcoal cloth is 6-48K plain weave charcoal cloth, and wherein K represents tow thousand radicals;
(2) chemical gas-phase permeation compaction technology: adopt the graphite frock with the inside and outside typing of the three-dimensional structure heater precast body in the step (1); With propylene or natural gas be raw material high temperature 850-1200 ℃ of following cracking, three-dimensional structure heater precast body is carried out gas-phase permeation compaction handles;
(3) condition of high vacuum degree high temperature purification treatment technology: the density>=1.30g/cm of the three-dimensional structure heater precast body in the step (2) 3The time, in vaccum sensitive stove, said three-dimensional structure heater precast body being carried out the condition of high vacuum degree high temperature purification treatment, said high temperature is meant that temperature is 1500-2300 ℃, said condition of high vacuum degree is meant vacuum degree≤40Pa; Density<the 1.30g/cm of the three-dimensional structure heater in the step (2) 3The time, return to step (2); The resistivity of the charcoal/carbon/carbon heating body after the condition of high vacuum degree high temperature purification treatment is 25~60 μ Ω m;
(4) mechanical processing technique: to process drilling machine boring in the step (3) with milling machine through the charcoal/carbon/carbon heating body of condition of high vacuum degree high temperature purification treatment;
(5) chemical vapor deposited coatings being carried out on the charcoal after machining/carbon/carbon heating body surface in the step (4) handles; Promptly make high resistance and high-purity polycrystalline hydrogenation furnace with charcoal/carbon/carbon heating body; Said high resistance is meant that resistance value is 0.06~0.25 Ω; Said high-purity is meant ash content≤800ppm, and the treatment temperature of said surface chemistry vapour deposition coating is 900-1200 ℃.
2. according to the preparation method of the described a kind of polysilicon hydrogenation furnace of claim 1 with charcoal/carbon/carbon heating body, it is characterized in that: the width of said charcoal/carbon/carbon heating body is 60~200mm, highly is 1000~4000mm.
CN2008102365461A 2008-12-31 2008-12-31 Carbon/carbon heating body preparation method for polysilicon hydrogenation furnace Active CN101478841B (en)