CN100999875A - Acrylate emulsifying thickening agent and production process thereof - Google Patents
Acrylate emulsifying thickening agent and production process thereof Download PDFInfo
- Publication number
- CN100999875A CN100999875A CN 200610045656 CN200610045656A CN100999875A CN 100999875 A CN100999875 A CN 100999875A CN 200610045656 CN200610045656 CN 200610045656 CN 200610045656 A CN200610045656 A CN 200610045656A CN 100999875 A CN100999875 A CN 100999875A
- Authority
- CN
- China
- Prior art keywords
- grams
- add
- gram
- weight portions
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Name of product | 5 minutes height (cm) | 10 minutes height (cm) | 30 minutes height (cm) |
The present invention | 0.025 | 0.036 | 0.05 |
DM-5622 | 0.26 | 0.30 | 0.35 |
Name of product | 5 minutes height (cm) | 10 minutes height (cm) | 30 minutes height (cm) |
HIT | 0.23 | 0.29 | 0.37 |
The present invention | 0.025 | 0.036 | 0.05 |
Claims (3)