BR112014015440A8 - chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma - Google Patents

chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma

Info

Publication number
BR112014015440A8
BR112014015440A8 BR112014015440A BR112014015440A BR112014015440A8 BR 112014015440 A8 BR112014015440 A8 BR 112014015440A8 BR 112014015440 A BR112014015440 A BR 112014015440A BR 112014015440 A BR112014015440 A BR 112014015440A BR 112014015440 A8 BR112014015440 A8 BR 112014015440A8
Authority
BR
Brazil
Prior art keywords
hot
low temperature
corrosion resistance
steel sheet
temperature toughness
Prior art date
Application number
BR112014015440A
Other languages
English (en)
Other versions
BR112014015440A2 (pt
Inventor
Sato Hironori
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of BR112014015440A2 publication Critical patent/BR112014015440A2/pt
Publication of BR112014015440A8 publication Critical patent/BR112014015440A8/pt

Abstract

resumo patente de invenção: "chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma". a presente invenção refere-se a uma chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem tendo uma resistência à tração de 340 mpa ou mais e menos que 540 mpa, uma capacidade de prensagem capaz de ser aplicada a um tanque de combustível, excelente resistência à fragilidade do trabalho secundário e tenacidade a baixa temperatura de uma zona de soldagem com costura, e excelente resistência á corrosão, a referida chapa tendo uma camada revestida por imersão a quente na superfície de uma chapa de aço laminada a frio, a chapa de aço laminada a frio contendo, em % em massa, c: 0,0005 a 0,0050%, si: 0,30% ou menos, mn: 0,70 a 3,00%, p: 0,05% ou menos, ti: 0,01 a 0,05%, nb: 0,01 a 0,04%, b: 0,0005 a 0,0030%, s: 0,01% ou menos, al: 0,01 a 0,30%, n: 0,0005 a 0,010%, e um saldo composto de fe e as inevitáveis impurezas. 21620260v1 1/1 21620260v1
BR112014015440A 2011-12-27 2012-12-18 chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma BR112014015440A8 (pt)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011286376 2011-12-27
PCT/JP2012/082845 WO2013099712A1 (ja) 2011-12-27 2012-12-18 低温靭性と耐食性に優れたプレス加工用溶融めっき高強度鋼板とその製造方法

Publications (2)

Publication Number Publication Date
BR112014015440A2 BR112014015440A2 (pt) 2017-06-13
BR112014015440A8 true BR112014015440A8 (pt) 2017-07-04

Family

ID=48697204

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112014015440A BR112014015440A8 (pt) 2011-12-27 2012-12-18 chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma

Country Status (8)

Country Link
US (1) US20140370330A1 (pt)
JP (1) JP5574061B2 (pt)
KR (1) KR20140095101A (pt)
CN (1) CN104011243B (pt)
BR (1) BR112014015440A8 (pt)
MX (1) MX362214B (pt)
TW (1) TWI479030B (pt)
WO (1) WO2013099712A1 (pt)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6264861B2 (ja) * 2013-11-27 2018-01-24 新日鐵住金株式会社 加工性に優れた高ヤング率冷延鋼鈑、電気亜鉛系めっき冷延鋼板、溶融亜鉛めっき冷延鋼板、合金化溶融亜鉛めっき冷延鋼板、及び、それらの製造方法
EP3342893A4 (en) * 2015-08-24 2019-01-16 Nippon Steel & Sumitomo Metal Corporation ALLOY-FILLED ZINC PLATED STEEL SHEET AND METHOD FOR MANUFACTURING SAME
CN106906415A (zh) * 2015-12-23 2017-06-30 本钢板材股份有限公司 一种改善冷轧if加磷高强钢脆性转变温度的方法
WO2019082037A1 (en) * 2017-10-24 2019-05-02 Arcelormittal PROCESS FOR MANUFACTURING COATED STEEL SHEET, TWO STITCHED SHEET METAL SHEETS, AND USE THEREOF
WO2018115946A1 (en) * 2016-12-21 2018-06-28 Arcelormittal A method for the manufacture of a coated steel sheet
EP3701056B1 (en) 2017-10-24 2021-12-01 ArcelorMittal A method for the manufacture of a coated steel sheet
WO2018115948A1 (en) * 2016-12-21 2018-06-28 Arcelormittal A method for the manufacture of a coated steel sheet
WO2019082036A1 (en) * 2017-10-24 2019-05-02 Arcelormittal METHOD FOR MANUFACTURING COATED STEEL SHEET
WO2018115947A1 (en) * 2016-12-21 2018-06-28 Arcelormittal A method for the manufacture of a coated steel sheet
CA3076464C (en) 2017-10-24 2022-07-12 Arcelormittal A method for the manufacture of a galvannealed steel sheet
CN111356783B (zh) 2017-11-17 2023-03-21 安赛乐米塔尔公司 用于制造抗液态金属脆化的锌涂覆的钢板的方法
KR102398869B1 (ko) * 2018-03-30 2022-05-16 제이에프이 스틸 가부시키가이샤 냉연 강판 및 그의 제조 방법
CN113490759B (zh) * 2019-04-01 2022-10-04 日本制铁株式会社 热冲压成形品及其制造方法
CN114000060B (zh) * 2021-11-10 2022-12-09 山东钢铁集团日照有限公司 一种高强度抗低温冲击含磷高强钢带的生产方法
CN116179935A (zh) * 2021-11-29 2023-05-30 上海梅山钢铁股份有限公司 抗拉强度360MPa级冷凝管用冷轧钢板及其生产方法

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6347338A (ja) * 1986-08-15 1988-02-29 Sumitomo Metal Ind Ltd 高張力溶融亜鉛めつき鋼板の製造方法
JPH0466621A (ja) * 1990-07-07 1992-03-03 Kobe Steel Ltd 耐２次加工脆性に優れた深絞り用熱延鋼板の製造方法
JP3293681B2 (ja) * 1993-04-01 2002-06-17 川崎製鉄株式会社 溶融亜鉛めっきまたは合金化溶融亜鉛めっき高強度鋼板およびその製造方法
JP4687260B2 (ja) * 2005-06-10 2011-05-25 Ｊｆｅスチール株式会社 表面性状に優れた深絞り用高張力冷延鋼板の製造方法
RU2430185C2 (ru) * 2007-04-11 2011-09-27 Ниппон Стил Корпорейшн Высокопрочная листовая сталь с покрытием, полученным горячим погружением, имеющая высокую ударную вязкость при низких температурах, для использования в штамповке и способ ее производства
JP5157749B2 (ja) * 2008-08-25 2013-03-06 新日鐵住金株式会社 溶接変形が小さい鋼板

Also Published As

Publication number Publication date
US20140370330A1 (en) 2014-12-18
WO2013099712A1 (ja) 2013-07-04
CN104011243B (zh) 2016-02-03
MX2014007786A (es) 2014-07-30
CN104011243A (zh) 2014-08-27
KR20140095101A (ko) 2014-07-31
JP5574061B2 (ja) 2014-08-20
JPWO2013099712A1 (ja) 2015-05-07
TWI479030B (zh) 2015-04-01
TW201333217A (zh) 2013-08-16
BR112014015440A2 (pt) 2017-06-13
MX362214B (es) 2019-01-09

Similar Documents

Publication Publication Date Title
BR112014015440A8 (pt) chapa de aço de alta resistência revestida por imersão a quente para trabalho de prensagem excelente em tenacidade a baixa temperatura e resistência à corrosão e método para produção da mesma
BR112012018552A2 (pt) chapa de aço laminada a frio de alta resistência e método de produção da mesma
BR112014002875A2 (pt) chapa de aço laminada a quente de alta razão de rendimento que tem excelente absorção de energia de impacto à baixa temperatura e resistência de amolecimento da haz, e método de produção da mesma
BR112015005216A2 (pt) Liga de aço para aço de alta resistência e baixa liga
BR112014007432A2 (pt) folha de aço galvanizada e método de fabricação da mesma
BR112012031722A2 (pt) aço estampado por calor, método de produção de chapa de aço para estampagem por calor, e método de produção de aço estampado por calor
MX2009010538A (es) Lamina de acero de alta resistentcia enchapada en caliente por inmersion para uso en estampacion, superior en tenacidad a baja temperatura y metodo de produccion de la misma.
BR112018012538A2 (pt) método para produzir uma folha de aço revestida, processo para produzir uma solda por pontos de resistência de pelo menos duas folhas de aço, folha de aço revestida, uso de uma folha de aço e uso de uma solda por pontos de resistência
BRPI0614391B8 (pt) composição para a produção de aço, chapa de aço, processos para produção de uma chapa laminada à quente e à frio e uso de uma chapa de aço.
BR112014000376A2 (pt) chapa de aço de resistência ultra-alta, resistente ao desgaste, e método de produção da mesma
BR112014007496A2 (pt) chapa de aço galvanizada por imersão a quente de alta resistência e chapa de aço galvanizada por imersão a quente ligada de alta resistência tendo excelente adesão de revestimento, capacidade de conformação e capacidade de expansão de furo com resistência à tração de 980 mpa ou mais e método para sua produção
BR112016001258A2 (pt) Chapa de aço laminada, processo de fabricação de uma chapa de aço, processo de fabricação de uma peça a partir de uma chapa e uso de uma chapa laminada
BR112013023792A2 (pt) chapa de aço para elemento gravado a quente e método de produção da mesma
BR112013031500B8 (pt) chapa de aço laminada a frio revestida, processo de fabricação uma chapa laminada a frio e revestida processo de fabricação de uma peça por soldagem de pelo menos uma chapa laminada a frio revestida e uso de uma chapa de aço laminada a frio revestida
BR112014002198A2 (pt) chapa de aço de alta resistência e chapa de aço galvanizada de alta resistência excelentes em capacidade de conformação e métodos de produção das mesmas
BR112015032233A2 (pt) folhas de aço, métodos de fabricação de folhas de aço e veículo
BR112012020133A2 (pt) chapa de aço de alta resistência e método para sua produção
BR112014000074A2 (pt) "chapa de aço laminada a frio galvanizada por imersão a quente, e processo para produção da mesma"
MY174534A (en) Steel sheet hot-dip coated with zn-al-mg-based system having excellent workability and method for manufacturing same
BR112014027992A2 (pt) peça de chassi automotivo fabricada a partir de chapa de aço laminada a quente conformável de alta resistência
BR112014005641A2 (pt) tira de aço galvanizada por imersão a quente de alta resistência
BR112014019497A8 (pt) Chapa de aço laminada a frio, chapa de aço revestida, e métodos para produção das mesmas
WO2007082786A8 (de) Verzinktes walzhartes kaltgewalztes flachprodukt und verfahren zu seiner herstellung
BR112018071948A2 (pt) placa de aço de alta resistência
ATE453733T1 (de) Werkstück aus einer hochfesten stahllegierung und dessen verwendung

Legal Events

Date Code Title Description
B350 Update of information on the portal [chapter 15.35 patent gazette]
B08F Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette]

Free format text: REFERENTE A 9A ANUIDADE.

B08H Application fees: decision cancelled [chapter 8.8 patent gazette]

Free format text: ANULADA A PUBLICACAO CODIGO 8.6 NA RPI NO 2649 DE 13/10/2021.

B25E Requested change of name of applicant rejected

Owner name: NIPPON STEEL AND SUMITOMO METAL CORPORATION (JP)

Free format text: INDEFERIDO O PEDIDO DE ALTERACAO DE NOME CONTIDO NA PETICAO 870190068900 DE19/07/2019 DEVIDO AO DESPACHO PUBLICADO NA RPI 2737 DE 20/06/2023.